We used Zr66.7Ni33.3 binary alloys as base alloys and selected the intermetallic compound TiC as additional particles. The influence of TiC addition on the microstructural evolution induced by mechanical alloying has been investigated using X-ray diffraction (XRD), scanning electron microscopy (SEM)，transmission electron microscopy (TEM), and differential scanning calorimetry (DSC). The experimental results show that the proper addition of TiC (5wt%) not only shortens the starting time of the amorphization reaction, but also improves the glass forming ability (GFA) of Zr-Ni alloy powders and greatly enhances the mechanical stability of the amorphous composites. Based upon the EDX analysis, we have found that the diffusion of TiC among the atoms of Zr and Ni is inhomogeneous, leading to the increase of the disorder degree of atoms in local regions. Therefore, the TiC addition improves the GFA and stability of the Zr-Ni alloys. The DSC results demonstrate that the effect of the addition of 3 wt% TiC is better than that of the addition of 5 wt% TiC on the improvement of thermal stability of the amorphous phase, suggesting that there is no correlation between thermal stability and mechanical stability of MA induced Zr-Ni-based amorphous alloys