The existence form of trace Er in Al-Zn-Mg-Cu alloy and its "Genetic Effect"
Author:
Affiliation:

Light Alloy Research Institute,Central South University

Fund Project:

  • 摘要
  • |
  • 图/表
  • |
  • 访问统计
  • |
  • 参考文献
  • |
  • 相似文献
  • |
  • 引证文献
  • |
  • 资源附件
  • |
  • 文章评论
    摘要:

    采用铁模铸造制备Al-Zn-Mg-Cu及Al-Zn-Mg-Cu-0.15% Er两种合金铸锭。利用光学显微镜(OM)、扫描电镜(SEM)及能谱分析(EDS)、差热分析(DSC)、透射电镜(TEM)、X射线衍射分析(XRD)和常温拉伸等方法研究了Er元素在Al-Zn-Mg-Cu合金铸态组织、均匀化态组织、变形组织以及时效态组织中的存在形式、作用机理以及其对合金室温拉伸性能的影响。研究结果表明: 微量Er元素对Al-Zn-Mg-Cu合金铸态组织有一定细化作用,但这种作用较为有限。Er在合金中主要以三元Al8Cu4Er相的形式存在,该相在合金凝固过程中形成并偏聚在晶界附近,常出现在共晶网状结构之间。此外,还有少量的Er生成了细小Al3Er粒子。Al8Cu4Er相熔点约为573.8°C,为难溶硬脆第二相,在合金变形过程中易破碎从而会导致裂纹萌生或成为粒子诱发再结晶形核的核心,最终会对合金的综合力学性能产生不利的影响。

    Abstract:

    Two kinds of alloys Al-Zn-Mg-Cu and Al-Zn-Mg-Cu-0.15% Er were prepared by steel mould casting. The existence and form of the Er in the as-cast, homogenized, deformed and aged microstructures of the Al-Zn-Mg-Cu alloy were investigated by optical microscopy (OM), scanning electron microscopy (SEM), energy dispersive spectrometer (EDS), differential scanning calorimetry (DSC), transmission electron microscopy(TEM), X-ray diffractometry (XRD). In addition, its effect on the tensile properties of the alloy at room temperature has also been discussed in detail. The results show that trace element Er can refine the as-cast microstructure of Al-Zn-Mg-Cu alloy to a certain extent, but this refinement is limited. Er exists in the alloy mainly in the form of a ternary Al8Cu4Er phase, which forms during the solidification and segregates at the grain boundaries, and often occurs between eutectic networks. Al8Cu4Er has a high melting point and poor plasticity and is therefore easily crushed during the thermal deformation of the alloy. Al8Cu4Er fragments may cause cracks and may also induce recrystallization nucleation, which will eventually have an adverse effect on the comprehensive properties of the alloy.

    参考文献
    相似文献
    引证文献
引用本文

黄元春,张传超,任贤魏,刘宇,陈斯卓,王艳玲.微量Er在高强Al-Zn-Mg-Cu合金中的存在形式及其“遗传效应”[J].稀有金属材料与工程,2019,48(9):2848~2856.[Yuanchun Huang, Chuanchao Zhang, Xianwei Ren, Yu Liu, Sizhuo Chen, Yanling Wang. The existence form of trace Er in Al-Zn-Mg-Cu alloy and its "Genetic Effect"[J]. Rare Metal Materials and Engineering,2019,48(9):2848~2856.]
DOI:10.12442/j. issn.1002-185X.20180577

复制
文章指标
  • 点击次数:
  • 下载次数:
  • HTML阅读次数:
  • 引用次数:
历史
  • 收稿日期:2018-05-31
  • 最后修改日期:2018-07-06
  • 录用日期:2018-07-27
  • 在线发布日期: 2019-10-09
  • 出版日期: