LZO对热障涂层中粘结层氧化的抑制行为研究
作者:
作者单位:

兰州理工大学 有色金属先进加工与再利用国家重点实验室

作者简介:

通讯作者:

中图分类号:

TG174.442

基金项目:

国家国际科技合作项目(2015DFR51090); 甘肃省重点研发计划项目(17YF1WA159)、科技特派计划(17JR7WA017)


Study on the inhibition behavior of LZO on the oxidation of bond coat in Thermal Barrier Coatings
Author:
Affiliation:

1.Lanzhou University of Technology,State Key Laboratory of Advanced Processing and Recycling of Nonferrous Metals,Gan su Lanzhou 730050;2.China

Fund Project:

International science and technology cooperation program of China(2015DFR51090);Key Research and Development project in Gansu(17YF1WA159)、Technology Special Plan (17JR7WA017)

  • 摘要
  • |
  • 图/表
  • |
  • 访问统计
  • |
  • 参考文献
  • |
  • 相似文献
  • |
  • 引证文献
  • |
  • 资源附件
  • |
  • 文章评论
    摘要:

    为了阐明LZO对热障涂层(TBCs)中粘结层氧化的抑制作用,利用爆炸喷涂(D-gun)在310S基体上制备NiCoCrAlY粘结层,大气等离子(APS)制备单陶瓷8YSZ涂层和双陶瓷LZO/8YSZ涂层。采用SEM、EDS和XRD表征了不同结构TBCs喷涂态及高温氧化后的微观组织和相结构。结果表明:1100 ℃下等温氧化(100小时)后双陶瓷LZO/8YSZ与单陶瓷8YSZ热障涂层相对氧化增重分别为2.82 mg/cm<sub>2</sub>和3.13 mg/cm<sub>2</sub>,TGO生长速率常数K<sub>p</sub>分别为5.79×10<sub>-2 </sub>μm<sub>2</sub>/h和6.26×10<sub>-2 </sub>μm<sub>2</sub>/h,厚度分布范围分别为3.75-5.25 μm和5-5.5 μm。相比单陶瓷TBCs,LZO/8YSZ双陶瓷TBCs中粘结层表现出氧化增重少、TGO生长速率低、粘结层中β相转变慢等明显特征。

    Abstract:

    In order to clarify the inhibitory effect of LZO on the oxidation of bond-coat in thermal barrier coatings (TBCs), NiCoCrAlY bond-coat was deposited on 310S substrate by Detonation gun spraying, and single ceramic 8YSZ coating and LZO/8YSZ double ceramic coating were deposited by air plasma spraying technology. The microstructure and phase structure of TBCs before and after high temperature oxidation were analyzed by SEM, EDS and XRD. The results showed that the relative oxidation weight gain of the double ceramic LZO/8YSZ and the single ceramic 8YSZ structure was 2.82 mg/cm2 and 3.13 mg/cm2, respectively. Corresponding the TGO growth rate constant Kp was 5.79 ×10- 2 μm2 / h and 6.26×10- 2 μm2 / h, respectively. And the corresponding thickness distribution range was 3.75-5.25 μm and 5-5.5 μm, respectively after isothermal oxidation (100 hours) at 1100 °C. Compared with the single ceramic 8YSZ TBCs, TGO exhibited obvious characteristics were less oxidation weight gain, low growth rate, and slow β phase transition in bond-coat of the LZO/8YSZ double ceramic TBCs.

    参考文献
    相似文献
    引证文献
引用本文

李文生,杨乐馨,安国升,成波,冯力,张义. LZO对热障涂层中粘结层氧化的抑制行为研究[J].稀有金属材料与工程,2019,48(11):3527~3534.[Li Wensheng, Yang Lexin, An Guosheng, Cheng Bo, Feng Li, Zhang Yi. Study on the inhibition behavior of LZO on the oxidation of bond coat in Thermal Barrier Coatings[J]. Rare Metal Materials and Engineering,2019,48(11):3527~3534.]
DOI:10.12442/j. issn.1002-185X.20180784

复制
文章指标
  • 点击次数:
  • 下载次数:
  • HTML阅读次数:
  • 引用次数:
历史
  • 收稿日期:2018-07-20
  • 最后修改日期:2018-08-17
  • 录用日期:2018-08-30
  • 在线发布日期: 2019-12-10
  • 出版日期: