Thermoelectric properties of nanostructured CoSb3 fast prepared by solid-state reaction
Author:
Affiliation:

1.College of Materials and Metallurgy,Guizhou University,Guiyang;2.School of Chemistry and Materials Engineering,Liupanshui Normal University,Liupanshui

Fund Project:

Guizhou provincial department of education fund project No. QianjiaoheKYzi[2016]102; The National Natural Science Foundation of China No. 51764005.

  • 摘要
  • |
  • 图/表
  • |
  • 访问统计
  • |
  • 参考文献
  • |
  • 相似文献
  • |
  • 引证文献
  • |
  • 资源附件
  • |
  • 文章评论
    摘要:

    采用固相反应法成功合成了具有纳米结构的p型COSb3。样品的物相组成和晶体结构采用XRD和SEM进行了表征。在室温下对不同温度和保温时间制备的样品进行了电学性质测试,选择了室温功率因子较好的样品,研究了不同温度下的热电性能。研究结果表明:采用球磨结合固相反法应制备可以制备单相的方钴矿热电材料,所制备的样品内部含有孔径均匀微气孔,晶粒尺寸在纳米范围。当制备温度为863 K时,样品获得最大塞贝克系数222.64 μV/k。当测试温度570 K时,样品获得最大功率因子132.17 μW/(mK2)。当样品制备温度903 K时,在600 K时得到最大的热电优值ZT~0.053。本研究为方钴矿热电材料的快速制备提供了一种新的技术途径。

    Abstract:

    P-type with nanostructured CoSb3 was successfully synthesized by solid-state reaction method. The phase composition and crystallographic structure were characterized by X-ray diffraction and scanning electron microscopy. The electrical properties of the samples prepared at different temperatures and holding time were tested at room temperature. The samples with better power factor at room temperature were selected to study the thermoelectric properties at different temperatures. The results show that the single phase Skutterudite thermoelectric materials can be prepared by ball milling combined with solid-state reaction. The samples have many micron-size pores uniformly and the grain was in the nanometer range. The maximum Seebeck coefficient was 222.64 μV/k obtained at the prepared temperature of 863 K. The maximum power factor of 132.17 μW/ (mK2) at 570 K was obtained and the maximum figure of merit, ZT~0.053 at 600 K was obtained by the sample which prepared temperature of 903 K. This study provides a new technology for the rapid preparation of Skutterudite thermoelectric materials.

    参考文献
    相似文献
    引证文献
引用本文

秦丙克,籍永华,白志玲,黄润,张金柱.固相反应法快速制备纳米结构的CoSb3及其热电性能[J].稀有金属材料与工程,2019,48(10):3118~3123.[Bingke Qin, Yonghua Ji, Zhiling Bai, Run Huang, Jinzhu Zhang. Thermoelectric properties of nanostructured CoSb3 fast prepared by solid-state reaction[J]. Rare Metal Materials and Engineering,2019,48(10):3118~3123.]
DOI:10.12442/j. issn.1002-185X.20180999

复制
文章指标
  • 点击次数:
  • 下载次数:
  • HTML阅读次数:
  • 引用次数:
历史
  • 收稿日期:2018-09-28
  • 最后修改日期:2019-09-19
  • 录用日期:2019-02-21
  • 在线发布日期: 2019-11-01
  • 出版日期: