Corrosion Behavior of WC-Co-(Ni)-(Cr) Cemented Carbide in Neutral Solution
Author:
Affiliation:

State Key Laboratory for Cemented Carbide

Fund Project:

  • 摘要
  • |
  • 图/表
  • |
  • 访问统计
  • |
  • 参考文献
  • |
  • 相似文献
  • |
  • 引证文献
  • |
  • 资源附件
  • |
  • 文章评论
    摘要:

    本文以WC粉、Co粉、Ni粉及Cr3C2粉为原料,采用粉末冶金方法制备了三组不同粘结相成分的WC-Co-(Ni)-(Cr)硬质合金,通过极化曲线测试和浸泡实验研究了三组合金在中性溶液中的腐蚀行为,并采用扫描电镜、能谱分析、X射线光电子能谱(XPS)和EBSD等手段对其腐蚀机理进行了探讨。结果表明,WC-Co和WC-Co-Cr硬质合金在中性溶液中主要发生粘结相Co的腐蚀,浸泡产生的腐蚀产物主要是Co(OH)2;添加Cr将提高WC-Co硬质合金在中性溶液中的耐腐蚀性能,这可能与Cr的添加明显降低了粘结相中密排六方Co的含量有关;同时添加Ni和Cr可进一步提高WC-Co合金在中性溶液中的耐腐蚀性能,在pH=7的Na2SO4溶液中浸泡480h后,WC-Co-Ni-Cr合金发生很少量的腐蚀。

    Abstract:

    Three groups of WC-Co-(Ni)-(Cr) cemented carbides with different binder phase compositions were prepared by powder metallurgy using WC, Co, Ni and Cr3C2 powders as raw materials. The corrosion behavior of the three alloys in neutral solution was studied by polarization curve test and immersion experiment. The corrosion mechanism was discussed by means of scanning electron microscopy, energy spectrum analysis, X-ray photoelectron spectroscopy (XPS) and EBSD. The results show that in neutral solution the corrosion of WC-Co and WC-Co-Cr cemented carbides is mainly caused by the selective dissolution of Co and the corrosion products after immersion are mainly composed of Co(OH)2. The corrosion resistance of WC-Co cemented carbide in neutral solution can be improved by the addition of Cr, which may be related to the decrease of the content of hcp-Co in the binder phase by adding Cr. Adding Ni and Cr together can further improve the corrosion resistance of WC-Co cemented carbide in neutral solution. After 480 hours immersion in Na2SO4 solution, the WC-Co-Ni-Cr alloy sample is just corroded slightly.

    参考文献
    相似文献
    引证文献
引用本文

魏修宇,金鹏,夏艳萍,余怀民,张卫兵. WC-Co-(Ni)-(Cr)硬质合金中性溶液中的腐蚀行为[J].稀有金属材料与工程,2020,49(1):313~319.[Wei Xiuyu, Jin Peng, Xia Yanping, Yu Huaimin, Zhang Weibing. Corrosion Behavior of WC-Co-(Ni)-(Cr) Cemented Carbide in Neutral Solution[J]. Rare Metal Materials and Engineering,2020,49(1):313~319.]
DOI:10.12442/j. issn.1002-185X.20181248

复制
文章指标
  • 点击次数:
  • 下载次数:
  • HTML阅读次数:
  • 引用次数:
历史
  • 收稿日期:2018-12-14
  • 最后修改日期:2019-03-21
  • 录用日期:2019-04-10
  • 在线发布日期: 2020-02-16
  • 出版日期: