Ce17Fe78-xB6Mx (M=Cu, Al, Ga; x=0-1.0)快淬合金永磁性能研究
作者:
作者单位:

江西省稀土磁性材料及器件重点实验室/江西理工大学稀土磁性材料及器件研究所

作者简介:

通讯作者:

中图分类号:

基金项目:

国家自然科学基金(项目号51564037,51661011),江西省教育厅青年(项目号GJJ180472)


Permanent magnetic properties of rapidly quenched Ce17Fe78-xB6Mx (M=Cu, Al, Ga; x=0-1.0) alloys
Author:
Affiliation:

Fund Project:

  • 摘要
  • |
  • 图/表
  • |
  • 访问统计
  • |
  • 参考文献
  • |
  • 相似文献
  • |
  • 引证文献
  • |
  • 资源附件
  • |
  • 文章评论
    摘要:

    本文基于熔体快淬技术,研究了低熔点元素Cu、Al和Ga添加对Ce17Fe78B6合金磁性能的影响。三类低熔点元素的加入,均降低了合金的磁化强度,而矫顽力有一定程度的提升。其中,Cu和Ga元素添加可优化晶粒尺寸分布,且Ga添加对Ce17Fe78B6合金矫顽力的提升最为有效。研究发现,Ce17Fe78B6合金回复曲线轻微开口;当Ga添加量为0.75 at.%时,合金具有较优异的综合磁性能,回复曲线完全闭合。适量Ga元素添加明显增强了Ce-Fe-B基合金晶间短程交换耦合作用,减小了合金平均回复磁导率,有效降低了Ce-Fe-B基合金在周期性反向磁场中的能量损失。

    Abstract:

    The effects of low melting point elements Cu, Al and Ga on the magnetic properties of Ce17Fe78B6 alloys prepared by melt spinning technique are studied. The addition of these elements decreases the saturation magnetization, while the coercivity increases to a certain extent. Among the additive elements, the addition of Cu and Ga optimize grain size distribution, Ga addition is the most effective way to improve the coercivity of Ce17Fe78B6 alloy. The recoil loop of Ce17Fe78B6 alloy is slightly open. The best overall magnetic properties are obtained for Ce17Fe77.25B6Ga0.75 alloy. Compared with the counterpart Ce-Fe-B alloy, the exchange coupling interaction between the grains of Ce-Fe-B-Ga alloy is enhanced. The recoil loops closes completely and the average recovery permeability decreases, which effectively enhances the resistance of Ce-Fe-B based alloys to external magnetic field interference.

    参考文献
    相似文献
    引证文献
引用本文

江庆政,何伦可,Sajjad Ur Rehman,宋杰,欧阳涵,钟震晨. Ce17Fe78-xB6Mx (M=Cu, Al, Ga; x=0-1.0)快淬合金永磁性能研究[J].稀有金属材料与工程,2019,48(11):3686~3692.[Jiang Qingzheng, He Lunke, Sajjad Ur Rehman, Song Jie, Ouyang Han, Zhong Zhenchen. Permanent magnetic properties of rapidly quenched Ce17Fe78-xB6Mx (M=Cu, Al, Ga; x=0-1.0) alloys[J]. Rare Metal Materials and Engineering,2019,48(11):3686~3692.]
DOI:10.12442/j. issn.1002-185X.20190243

复制
文章指标
  • 点击次数:
  • 下载次数:
  • HTML阅读次数:
  • 引用次数:
历史
  • 收稿日期:2019-03-22
  • 最后修改日期:2019-05-30
  • 录用日期:2019-06-14
  • 在线发布日期: 2019-12-10
  • 出版日期: