Grain refinement and mechanical properties of Al-Cu-Ti alloys after different melt heat treatment processes
Author:
Affiliation:

University of Jinan

Fund Project:

National Natural Science Foundations of China (Grants Nos. 51772132);Natural Science Foundation of Shandong Province of China (ZR2019MEM019)

  • 摘要
  • |
  • 图/表
  • |
  • 访问统计
  • |
  • 参考文献
  • |
  • 相似文献
  • |
  • 引证文献
  • |
  • 资源附件
  • |
  • 文章评论
    摘要:

    本文研究了添加细化剂和不同热处理工艺(过热处理和热速处理)对Al-Cu合金的改性。分析了Al-Cu-Ti合金的相组成、凝固微观组织和力学性能。此外,采用差示扫描量热法(DSC)研究了Al-Cu-Ti合金在不同熔体热处理工艺后的熔体结构转变行为。实验结果表明,热速处理极大地细化了Al-Cu-Ti合金晶粒,且力学性能得到有效改善。通过对热力学相变分析,发现Al-Cu-Ti合金经过热处理和热速处理后的熔化潜热随着界面能的增大而变小,从而在一定程度上细化了合金的微观组织。

    Abstract:

    In this study, the modification of Al-Cu alloy by adding grain refiner combined with different heat treatments (superheat treatment and thermal rate treatment) is investigated. The phase composition, solidification microstructure and mechanical properties of Al-Cu-Ti alloys are analyzed. Moreover, the melt structure transformation of Al-Cu-Ti alloys after different melt heat treatments was studied by DSC. The experimental results showed that the thermal rate treatment greatly refined the grain of Al-Cu-Ti alloy and improved the mechanical properties. Through the analysis of thermodynamic phase transition, it was found that the latent heat of fusion of Al-Cu-Ti alloy after superheat treatment and thermal rate treatment became smaller due to the increase of interfacial energy, which leads to refine the microstructure of alloy to some extent.

    参考文献
    相似文献
    引证文献
引用本文

王琳,孙昱,薄琳,左敏,赵德刚.不同熔体热处理工艺后Al-Cu-Ti合金的晶粒细化及力学性能改善[J].稀有金属材料与工程,2020,49(8):2615~2622.[Wang Lin, Sun Yu, Bo Lin, Zuo Min, Zhao Degang. Grain refinement and mechanical properties of Al-Cu-Ti alloys after different melt heat treatment processes[J]. Rare Metal Materials and Engineering,2020,49(8):2615~2622.]
DOI:10.12442/j. issn.1002-185X.20190444

复制
文章指标
  • 点击次数:
  • 下载次数:
  • HTML阅读次数:
  • 引用次数:
历史
  • 收稿日期:2019-05-24
  • 最后修改日期:2019-08-18
  • 录用日期:2019-09-06
  • 在线发布日期: 2020-09-27
  • 出版日期: