激光沉积修复单道多层DZ125双级时效热处理组织与性能
作者:
作者单位:

1.沈阳航空航天大学航空制造工艺数字化国防重点学科实验室;2.沈阳工业大学,机械工程学院;3.中国航发沈阳黎明航空发动机有限责任公司焊接技术室

作者简介:

通讯作者:

中图分类号:

TG132.3+2

基金项目:

辽宁省自然科学基金(20170540690)国家重点研发计划资助(2017YFB1104002)


Microstructure and properties of laser deposition for single multilayer DZ125 two-stage aging heat treatment
Author:
Affiliation:

Fund Project:

Liaoning Natural Science Foundation(20170540690)National Key R&D Program Funding(2017YFB1104002)

  • 摘要
  • |
  • 图/表
  • |
  • 访问统计
  • |
  • 参考文献
  • |
  • 相似文献
  • |
  • 引证文献
  • |
  • 资源附件
  • |
  • 文章评论
    摘要:

    通过在DZ125铸造基体上沿纵向进行激光沉积单道多层实验,分析了DZ125沉积态与双级时效热处理试样的组织和性能。结果表明:沉积态修复区组织从底部到顶部分别为平面晶、柱状晶和等轴晶组织,修复区主要为MC碳化物,热影响区因热量的输入,MC分解为M23C6;与沉积态组织相比,双级时效热处理后,修复区组织形成了新的晶界,部分MC碳化物分解为M6C与M23C6,γ'相尺寸略有增大,约为600-800nm,分布均匀;热影响区碳化物尺寸略有减小,γ′相尺寸增大,呈立方体形状;双级时效热处理修复试样在1000℃下的抗拉强度为516MPa、屈服强度为386MPa,分别达到铸件的89.7%和97.7%,延伸率为13.6%,达到铸件的43.9%;热处理后修复试样的平均硬度为473HV0.3,高于沉积态试样平均硬度433HV0.3,且热处理态与沉积态试样沿修复区、热影响区到基体硬度呈降低趋势。

    Abstract:

    The microstructure and properties of DZ125 as-deposited and two-stage aging heat treated samples were analyzed by laser deposition single-layer multi-layer experiments on the casting substrate along the longitudinal direction of DZ125. The results show that the microstructure of the sedimentary repair area is planar crystal, columnar crystal and equiaxed crystal structure from the bottom to the top. The repaired area is mainly MC carbide. The heat affected zone will be decomposed into M23C6 by MC due to the input of heat. Compared with the microstructure, after the two-stage aging heat treatment, a new grain boundary is formed in the repaired area, and some MC carbides are decomposed into M6C and M23C6, and the γ" phase size is slightly increased, about 600-800 nm, and the distribution is uniform; The size of the carbides in the area is slightly reduced, the size of the γ" phase is still increasing, and it is cubic. The tensile strength of the two-stage aging heat treatment specimen at 1000 °C is 516 MPa, and the yield strength is 386 MPa, which is 89.7% of the casting respectively. And 97.7%, the elongation rate is 13.6%, reaching 43.9% of the casting; the average hardness of the repaired sample after heat treatment is 473 HV0.3, which is higher than the average hardness of the as-deposited sample 433 HV0.3, and the heat-treated state and the deposited sample along the repair zone, heat The hardness of the affected zone to the matrix is decreasing.

    参考文献
    相似文献
    引证文献
引用本文

卞宏友,翟星玥,王世杰,李英,王伟,王维.激光沉积修复单道多层DZ125双级时效热处理组织与性能[J].稀有金属材料与工程,2020,49(9):3122~3128.[bianhonhyou, zhaixingyue, wangshijie, liying, wangwei, wangwei. Microstructure and properties of laser deposition for single multilayer DZ125 two-stage aging heat treatment[J]. Rare Metal Materials and Engineering,2020,49(9):3122~3128.]
DOI:10.12442/j. issn.1002-185X.20190645

复制
文章指标
  • 点击次数:
  • 下载次数:
  • HTML阅读次数:
  • 引用次数:
历史
  • 收稿日期:2019-08-05
  • 最后修改日期:2019-10-15
  • 录用日期:2019-10-22
  • 在线发布日期: 2020-10-15
  • 出版日期: