Preparation and Antibacterial Properties of Ta2O5 Nanorods Doped with Copper on Tantalum
Author:
Affiliation:

Shaanxi University of Science and Technology,School of Material Science and Engineering,Shaanxi Key Laboratory of Green Preparation and Functionalization for Inorganic Materials,Xi’an,710021

Fund Project:

  • 摘要
  • |
  • 图/表
  • |
  • 访问统计
  • |
  • 参考文献
  • |
  • 相似文献
  • |
  • 引证文献
  • |
  • 资源附件
  • |
  • 文章评论
    摘要:

    本实验采用两步水热法在钽基体表面制备出掺杂Cu2+的Ta2O5纳米棒薄膜。采用XRD、SEM、XPS等方法分析了材料的物相和表面微观结构。用ICP检测了样品在生理盐水中离子析出浓度,最后通过平板计数法检验了不同含量铜掺杂Ta2O5薄膜的抗菌能力。结果表明,通过两步水热处理,在钽表面生成了简单斜方晶体结构的Ta2O5纳米棒阵列,Cu2+的掺杂不会对纳米棒薄膜的微观形貌和物相造成显著影响。随时间的增加,掺铜薄膜的铜离子析出速率逐渐趋于平缓。平板计数法表明,Cu2+ 的掺杂量达到2.68At%时,铜掺杂Ta2O5纳米棒薄膜的抗菌性能最好,抗菌率达99.2%。

    Abstract:

    Ta2O5 nanorod films doped with Cu2+ were prepared by a two-step hydrothermal method on tantalum. XRD, SEM and XPS were used to analyze the phase and surface microstructure of the materials. The ion precipitation concentration of samples in normal saline was detected by ICP, and the antibacterial ability of Ta2O5 films with different content of copper was tested by plate counting method. The results showed that Ta2O5 nanorods with simple rhombic crystal structure were generated on the tantalum surface by two-step hydrothermal treatment, and the doping of Cu2+ did not significantly affect the microstructure and phase of nanorods. With the increase of time, the precipitation rate of copper ions in copper-doped films gradually tends to be flat. The result of plate counting showed that when the doping amount of Cu2+ reached 2.68At%, copper doped Ta2O5 nanorod films had the best antibacterial performance and the antibacterial rate reached 99.2%.

    参考文献
    相似文献
    引证文献
引用本文

王翠翠,李新宇,童晨光,蔡安琦,郭宏伟,殷海荣.钽表面铜掺杂Ta2O5纳米棒的制备及抗菌性能研究[J].稀有金属材料与工程,2020,49(9):3163~3169.[Wang Cuicui, Li Xinyu, Tong Chenguang, Cai Anqi, Guo Hongwei, Yin Hairong. Preparation and Antibacterial Properties of Ta2O5 Nanorods Doped with Copper on Tantalum[J]. Rare Metal Materials and Engineering,2020,49(9):3163~3169.]
DOI:10.12442/j. issn.1002-185X.20190695

复制
文章指标
  • 点击次数:
  • 下载次数:
  • HTML阅读次数:
  • 引用次数:
历史
  • 收稿日期:2019-08-23
  • 最后修改日期:2019-09-28
  • 录用日期:2019-10-11
  • 在线发布日期: 2020-10-15
  • 出版日期: