Interfacial microstructure and shear strength of a Cu/Al bimetal fabricated by hot press welding
Author:
Affiliation:

Shaanxi Province Key Laboratory for Electrical Materials and Infiltration Technology,Xi’an University of Technology,Xi’an

Fund Project:

  • 摘要
  • |
  • 图/表
  • |
  • 访问统计
  • |
  • 参考文献
  • |
  • 相似文献
  • |
  • 引证文献
  • |
  • 资源附件
  • |
  • 文章评论
    摘要:

    采用扩散焊(DFW)技术制备了Cu/Al双金属,连接温度范围683-803K,连接时间范围20-80min,连接压力15MPa。Cu/Al双金属界面处的SEM试验结果表明,随着焊接温度的升高和保温时间的延长,界面层厚度逐渐增加,在连接温度为803K,连接时间80min,Cu/Al界面处形成了Al4Cu9,Al3Cu4,AlCu、Al2Cu金属间化合物(从铜侧到铝侧),根据扩散动力学,金属间化合物(IMCS)的生成顺序为Al2Cu、Al4Cu9、AlCu、Al3Cu4。Cu / Al双金属的剪切试验显示为脆性断裂,并且界面强度随着IMC的减少而增加。在723 K的焊接温度下进行20分钟焊接后,Cu / Al双金属的剪切强度最高为63.8 MPa。

    Abstract:

    Cu/Al bimetals were fabricated by diffusion welding (DFW) at welding temperatures ranging between 683 and 803 K, welding time between 20 and 80 min, and a welding pressure of 15 MPa. The scanning electron microscopy (SEM) and energy dispersive spectroscopy (EDS) results of the Cu/Al interface showed that the width of interface layer gradually increased with increasing welding temperature and prolonged welding time. Following welding at 803 K for 80 min, intermetallic compounds (IMCs) of Al4Cu9, Al3Cu4, AlCu, and Al2Cu occurred at the Cu/Al interface from the copper side to the aluminum side. The IMCs occurred in the sequence of Al2Cu, AlCu, Al3Cu4, and Al4Cu9 . Shear test of Cu/Al bimetal showed brittle facture, and the interfacial strength increased with lower amount of IMCs. A maximum shear strength of the Cu/Al bimetal of 63.8 MPa was obtained following DFW at a welding temperature of 723 K for 20 min.

    参考文献
    相似文献
    引证文献
引用本文

邹军涛,高磊,谢庭芳,李思林,孙利星,梁淑华.热压焊接制备的Cu / Al双金属的界面组织和剪切强度[J].稀有金属材料与工程,2020,49(12):4121~4128.[Juntao Zou, Lei Gao, Tingfang Xie, Silin Li, Lixing Sun, Shuhua Liang. Interfacial microstructure and shear strength of a Cu/Al bimetal fabricated by hot press welding[J]. Rare Metal Materials and Engineering,2020,49(12):4121~4128.]
DOI:10.12442/j. issn.1002-185X.20200380

复制
文章指标
  • 点击次数:
  • 下载次数:
  • HTML阅读次数:
  • 引用次数:
历史
  • 收稿日期:2020-06-02
  • 最后修改日期:2020-11-11
  • 录用日期:2020-07-01
  • 在线发布日期: 2021-01-13
  • 出版日期: