    摘要:

    采用熔体反应制备了组织均匀的Al-5Nb-RE-B中间合金,研究了该中间合金对A356铝合金的细化效果。结果表面,添加1 wt.%的Al-5Nb-RE-B中间合金后,A356铝合金的晶粒度从原来的800um细化为200um。不同冷速下的研究结果表明,Al-5Nb-RE-B中间合金具有较低的冷速敏感性。

    Abstract:

    The Al-5Nb-RE-B master alloy with a uniform microstructure has been prepared using melt reaction method. The effect of Al-5Nb-RE-B inoculation on aluminum alloy A356 for their grain refinement has been studied. It was found that the grain size of A356 alloy can be reduced from 800 μm to 200 μm by the addition of 1wt.% of the prepared Al-5Nb-RE-B master alloy. The in-depth analysis of the alloys solidified under wide range of cooling rates indicated that Al-5Nb-RE-B inoculation does not only lead to a much finer microstructural features but also makes the final grain size far less sensitive to the cooling rate employed to solidify the material.

    参考文献
    [1] Sha M, Wu S S, Wang X T, et al. Materials Science and Engineering: A [J], 2012, 35:258-263
    [2] Chen Z W, Ma C Y, Chen P. Transactions of Nonferrous Metals Society of China [J], 2012, 22(1):42-46
    [3]Nowak M, Bolzoni L, Hari B N, Materials Design (1980-2015) [J], 2015, 66: 366-375
    [4]Merlin M, Timeli G, Bonollo F et al. Journal of Materials Processing Technology [J], 2009, 209(2):1060-1073
    [5] La T, E A D et al. Journal of Rare Earths [J], 2013, 31(8): 811-816
    [6] Metan V, Eigenfeld K et al. Journal of Alloys and Compounds [J], 2009, 487(1-2): 163-172
    [7] Fan Z, Wang Y, Zhang Y et al. Acta Materialia [J], 2015, 84: 292-304
    [8] Bolzoni L, Nowak M, Hari B N. Materials Design (1980-2015) [J], 2015, 66: 376-383
    [9] Bolzoni L, Nowak M, Hari B N. Materials Science and Engineering: A [J], 2015, 628: 230-237
    [11] Bolzoni L, Nowak M, Hari Babu N. Journal of Alloys and Compounds [J], 2015, 623: 79-82
    [12] Wang X J, Xu C, Muhammad A et al. Transactions of Nonferrous Metals Society of China [J], 2014, 24(7): 2244-2250
    [13]Zhao H L, Song Y, Li M et al. Journal of Alloys and Compounds [J], 2010, 508(1): 206-211
    [14] Wang Z J, Si N C. Rare Metal Materials Engineering [J], 2015, 44(12): 2970-2975
    [15] Zhang H R, Liu Z B, Li Z Z et al. Acta Metallurgica Sinica (English Letters) [J], 2016. 29(5): 414-421
    引证文献
    网友评论
    网友评论
    分享到微博
    发 布
引用本文

武晓燕,张花蕊,张虎,姜峰.新型Al-5Nb-RE-B合金组织和细化效果研究[J].稀有金属材料与工程,2018,47(7):2017~2022.[Wu Xiaoyan, Zhang Huarui, Zhang Hu, Jiang Feng. Microstructure and grain refinement performance of a new Al-5Nb-RE-B master alloy[J]. Rare Metal Materials and Engineering,2018,47(7):2017~2022.]
DOI:[doi]

复制
文章指标
  • 点击次数:804
  • 下载次数: 881
  • HTML阅读次数: 148
  • 引用次数: 0
历史
  • 收稿日期:2016-11-05
  • 最后修改日期:2017-06-19
  • 录用日期:2017-06-26
  • 在线发布日期: 2018-10-10