TEM Study of Zirconium Hydrides Precipitated in Zr-4 Alloy
Author:
Affiliation:

University of Science and Technology Beijing 100083, China

Fund Project:

  • 摘要
  • |
  • 图/表
  • |
  • 访问统计
  • |
  • 参考文献
  • |
  • 相似文献
  • |
  • 引证文献
  • |
  • 资源附件
  • |
  • 文章评论
    摘要:

    利用透射电镜(TEM)研究了Zr-4合金吸氢后析出氢化物的类型、形貌及其位相关系。结果表明,随着吸氢量的增加,Zr-4合金中依次析出了δ-ZrH1.6及ε-ZrH1.8氢化物。δ氢化物主要以板条状从α-Zr 基体上析出,二者的取向关系为:(0001)α//(001)δ,[2 0]α //[110]δ。 ε氢化物以针状形貌从δ氢化物中析出,析出的ε氢化物的密排面( 1 )与δ氢化物的密排面( 1 )平行,二者的取向关系为:( 1 )δ //( 1 )ε,[ 12] δ//[011]ε。高分辨观察进一步表明,δ-ZrH1.6及ε-ZrH1.8氢化物的晶格点阵均出现了严重的扭曲变形,说明相变存在较大的应力集中。

    Abstract:

    The type, morphology and orientation relationship of the hydride precipitates in a hydrogen absorbed Zr-4 alloy have been studied by means of transmission electron microscopy (TEM). The results show that δ-ZrH1.6 and ε-ZrH1.8 hydrides are found to precipitate successively with the increase of hydrogen absorption. For the δ-ZrH1.6 hydrides, they are mainly in the form of lath and precipitate in the orientation relationship of (0001)α//(001)δ and [2 0]α //[110]δ with the α-Zr matrix, while for the ε-ZrH1.8 hydrides, they are in acicular morphology and precipitate in the orientation relationship of ( 1 )δ //( 1 )ε and [ 12] δ//[011]ε with the δ-ZrH1.6 hydrides. The close-packed planes of these two hydrides are identified to be parallel. High-resolution TEM observation shows that there exists a great deal of distortion inside the crystal lattice of the δ-ZrH1.6 and ε-ZrH1.8 hydrides, indicating a large stress concentration produced during their precipitation.

    参考文献
    相似文献
    引证文献
引用本文

窦娜娜. Zr-4合金中氢化物析出的TEM研究[J].稀有金属材料与工程,2016,45(1):97~101.[dounana. TEM Study of Zirconium Hydrides Precipitated in Zr-4 Alloy[J]. Rare Metal Materials and Engineering,2016,45(1):97~101.]
DOI:[doi]

复制
文章指标
  • 点击次数:
  • 下载次数:
  • HTML阅读次数:
  • 引用次数:
历史
  • 收稿日期:2014-01-22
  • 最后修改日期:2014-02-23
  • 录用日期:
  • 在线发布日期: 2019-01-04
  • 出版日期: