等离子喷涂(La0.4Sm0.5Yb0.1)2Zr2O7涂层的热性能研究
DOI:
作者:
作者单位:

北京理工大学材料学院,北京理工大学材料学院,北京理工大学材料学院,北京理工大学材料学院

作者简介:

通讯作者:

中图分类号:

基金项目:


Study on Thermal Properties of Plasma-Sprayed (La0.4Sm0.5Yb0.1)2Zr2O7 Coatings
Author:
Affiliation:

School of Materials Science and Engineering,Beijing Institute of Technology,School of Materials Science and Engineering,Beijing Institute of Technology,School of Materials Science and Engineering,Beijing Institute of Technology,School of Materials Science and Engineering,Beijing Institute of Technology

Fund Project:

  • 摘要
  • |
  • 图/表
  • |
  • 访问统计
  • |
  • 参考文献
  • |
  • 相似文献
  • |
  • 引证文献
  • |
  • 资源附件
  • |
  • 文章评论
    摘要:

    本文采用大气等离子喷涂制备了(La0.4Sm0.5Yb0.1)2Zr2O7涂层,并在相同的条件下制备了Sm2Zr2O7涂层作为对比。分别用扫描电子显微镜和X射线衍射仪分析 LSYZO涂层的微观形貌和相结构,并对两种涂层的热导率进行测定。结果表明,等离子喷涂后LSYZO涂层的相结构未发生变化。LSYZO涂层的结合强度为22 MPa,与SZO涂层相当。LSYZO涂层热震40次后发生失效,其热导率明显低于SZO涂层,这主要与LSYZO陶瓷自身的复杂结构有关。

    Abstract:

    (La0.4Sm0.5Yb0.1)2Zr2O7 (LSYZO) coating was prepared by atmospheric plasma spray. Sm2Zr2O7 (SZO) coating was also prepared in the same conditions as a contrast. Microstructures and phases of LSYZO coatings were investigated by scanning electrical microscopy and X-ray diffraction, respectively. The thermal conductivities of the two coatings were measured. The results show that the phase composition of LSYZO coating has no change after plasma spraying. The adhesion strength of LSYZO coating is 22 MPa, which is comparable with that of SZO coating. And LSYZO coating has lifetime of about 40 cycles. The thermal conductivity of LSYZO coating is lower than that of SZO coating, which mainly depends on the complex structure of LSYZO ceramic.

    参考文献
    相似文献
    引证文献
引用本文

刘玲,王富耻,马壮,孙英超.等离子喷涂(La0.4Sm0.5Yb0.1)2Zr2O7涂层的热性能研究[J].稀有金属材料与工程,2017,46(10):2785~2789.[Ling Liu, Fuchi Wang, Zhuang Ma, Yingchao Sun. Study on Thermal Properties of Plasma-Sprayed (La0.4Sm0.5Yb0.1)2Zr2O7 Coatings[J]. Rare Metal Materials and Engineering,2017,46(10):2785~2789.]
DOI:[doi]

复制
文章指标
  • 点击次数:
  • 下载次数:
  • HTML阅读次数:
  • 引用次数:
历史
  • 收稿日期:2015-09-29
  • 最后修改日期:2016-01-04
  • 录用日期:2016-03-29
  • 在线发布日期: 2017-12-01
  • 出版日期: