Structure and performance of KH570/A171 modified silica sol film on zirconium hydride surface
Author:
Affiliation:

General Research Institute for Nonferrous Metals,General Research Institute for Nonferrous Metals,General Research Institute for Nonferrous Metals,General Research Institute for Nonferrous Metals,General Research Institute for Nonferrous Metals,General Research Institute for Nonferrous Metals

Fund Project:

  • 摘要
  • |
  • 图/表
  • |
  • 访问统计
  • |
  • 参考文献
  • |
  • 相似文献
  • |
  • 引证文献
  • |
  • 资源附件
  • |
  • 文章评论
    摘要:

    以硅酸乙酯(TEOS)、γ-(甲基丙烯酰氧)丙基三甲氧基硅烷(硅烷偶联剂KH570)和乙烯基三甲氧基硅烷(硅烷偶联剂A171)等为主要原料制备硅烷偶联剂KH570/A171改性硅溶胶,进而采用浸渍提拉法在氢化锆表面制备溶胶膜层。红外光谱(FTIR)分析显示,硅烷偶联剂能有效参与溶胶共聚反应。透射电镜(TEM)分析表明,硅烷偶联剂的逐一加入有利于胶粒粒径细化,提高和维持胶粒之间亲和能力。扫描电镜(SEM)分析显示,使用硅烷偶联剂KH570和A171改性的有机硅溶胶,可在氢化锆表面制备干燥后无裂纹溶胶膜层,烧结溶胶膜层存在微裂纹而无明显崩落;溶胶膜层表面元素分布均匀,烧结后存在碳残余。真空热放氢实验表明,氢化锆表面烧结硅溶胶膜层的制备,起到了阻氢渗透的作用。600℃二氧化碳气氛中,烧结硅溶胶膜层具备阻碍氧渗透能力,对氢化锆基体有抗高温氧化作用。

    Abstract:

    Silane coupling agent modified silica sol was prepared with ethyl silicate (TEOS), 3-Methacryloxypropyltrimethoxysilane (silane coupling agent KH570) and vinyl trimethoxy silane (silane coupling agent A171) as main raw material, and then modified silica sol film on zirconium hydride was made by dip-coating method. FTIR analysis showed that coupling agent could participate in copolymerization reaction of the sol effectively. TEM analysis showed that it’s advantageous to refine colloidal particle size, improve and maintain the affinity between them as KH570 and A171 were added one by one into the sol. SEM analysis showed that dried crack-free sol film could be prepared on zirconium hydride substrate using KH570 and A171 modified silica sol. Micro cracks exist on the sintered sol film but without apparent flaking. Elements distribute evenly on the surface of the sol film in which residual carbon exists after sintering. Thermal hydrogen release experiment in vacuum demonstrated the preparation of sintered sol film on zirconium hydride could resistant hydrogen permeation. In CO2 atmosphere under 600℃, oxygen diffusion could also be hindered by the sintered silica sol film, which shows oxidation resistance for zirconium hydride substrate.

    参考文献
    相似文献
    引证文献
引用本文

吴明,陈洋,闫国庆,彭家庆,孙玉璞,王力军.氢化锆表面KH570/A171改性硅溶胶膜层结构及性能[J].稀有金属材料与工程,2018,47(2):630~635.[Wu Ming, Chen Yang, Yan Guoqing, Peng Jiaqing, Sun Yupu, Wang Lijun. Structure and performance of KH570/A171 modified silica sol film on zirconium hydride surface[J]. Rare Metal Materials and Engineering,2018,47(2):630~635.]
DOI:[doi]

复制
文章指标
  • 点击次数:
  • 下载次数:
  • HTML阅读次数:
  • 引用次数:
历史
  • 收稿日期:2016-01-07
  • 最后修改日期:2016-02-16
  • 录用日期:2016-03-30
  • 在线发布日期: 2018-03-15
  • 出版日期: