李家节,郭诚君,周头军,刘武杰,陈金水,刘仁辉,周慧杰,杨斌.热扩渗DyZn合金膜层对烧结钕铁硼磁性能与耐热性能的影响[J].稀有金属材料与工程,2018,47(3):995~1000.[Li Jiajie,Guo Chengjun,Zhou Toujun,Liu Wujie,Chen Jinshui,Liu Renhui,Zhou Huijie,Yang Bin.Effects of Thermal Diffusing DyZn Alloy Film on the Magnetic Properties and Heat Resistance for Sintered NdFeB Magnets[J].Rare Metal Materials and Engineering,2018,47(3):995~1000.]
热扩渗DyZn合金膜层对烧结钕铁硼磁性能与耐热性能的影响
投稿时间:2016-01-08  修订日期:2016-04-15
中文关键词:  共溅射  热扩渗  DyZn合金  烧结钕铁硼
基金项目:国家自然科学基金资助(项目号51561009);江西省高校科技落地计划项目(项目号KJLD14043);江西省青年科学基金计划项目(项目号20151BAB216005);江西省教育厅研究项目(项目号GJJ14448)
中文摘要:
      采用直流磁控溅射的方法,在烧结NdFeB磁体表面制备了DyZn薄膜,研究了热扩渗处理磁体前后的磁性能、温度稳定性及微观组织结构变化。晶界扩散渗DyZn处理后,磁体在保持剩磁基本不降低的情况下,矫顽力大幅度提升,矫顽力从原来的963.68kA/m提高到1544.60kA/m,增幅达63.31%。晶界扩散处理可以改善磁体的温度稳定性,在293K~453K范围内,剩磁温度系数基本不变,而矫顽力温度系数由-0.5533%/K降低为-0.4885%/K。通过对样品微观组织结构观察发现,Dy元素沿着晶界液相扩散,主要富集在晶界相和晶粒外延层处,晶界相结构与成分的优化,及晶界和晶粒之间(Nd,Dy)2Fe14B过渡层的形成,是矫顽力大幅度提升的主要原因。
Effects of Thermal Diffusing DyZn Alloy Film on the Magnetic Properties and Heat Resistance for Sintered NdFeB Magnets
英文关键词:Co-sputtering  Thermal diffusion  DyZn alloy  Sintered NdFeB
英文摘要:
      The DyZn films on the sintered NdFeB magnet surface were prepared through DC magnetron sputtering. The magnetic properties, temperature stability and microstructure of the magnets before and after the thermal diffusion treatment were compared. Under the circumstances of keeping the remanence invariable, the magnet coercivity enhanced significantly from 963.68 kA/m to 1544.60 kA/m with an increasing of 63.31% after DyZn thermal diffusion. The magnet temperature stability could be improved by grain boundary diffusion. The temperature coefficient of the remanence kept constant while that of the coercivity reduced from -0.5533% /K to -0.4885% /K in the range of 293K~453K. Dy elements diffusing along the grain boundary phase mainly aggregated between the grain boundary phase and the grain epitaxial layer via SEM and EPMA with EDS observation.The optimization of microstructure and composition of the grain boundary phase and the formed transition layer (Nd,Dy)2Fe14B between them are the main reasons which causing the coercivity to upgrade dramatically.
作者单位E-mail
李家节 江西理工大学工程研究院 江西 赣州 江西理工大学材料科学与工程学院 江西 赣州 lifest@163.com 
郭诚君 江西理工大学材料科学与工程学院 江西 赣州  
周头军 江西理工大学材料科学与工程学院 江西 赣州  
刘武杰 江西理工大学材料科学与工程学院 江西 赣州  
陈金水 江西理工大学材料科学与工程学院 江西 赣州  
刘仁辉 江西理工大学工程研究院 江西 赣州  
周慧杰 虔东稀土集团股份有限公司 江西 赣州  
杨斌 江西理工大学工程研究院 江西 赣州 江西理工大学材料科学与工程学院 江西 赣州  
摘要点击次数: 387
全文下载次数: 123
查看全文  查看/发表评论  下载PDF阅读器
关闭