王东鑫,乔印凯,刘东,华刚,王海滨,刘雪梅,宋晓艳.Hf、CNTs混合掺杂对纳米晶Sm5Co19合金结构和磁性能的影响[J].稀有金属材料与工程,2018,47(3):1001~1006.[wangdongxin,qiaoyinkai,liudong,huagang,wanghaibin,liuxuemei,songxiaoyan.Effect of Alloy Structure and the Magnetic Mix Doping Hf Elements and CNTs on Nanocrystalline Sm5Co19 Alloy[J].Rare Metal Materials and Engineering,2018,47(3):1001~1006.]
Hf、CNTs混合掺杂对纳米晶Sm5Co19合金结构和磁性能的影响
投稿时间:2016-01-13  修订日期:2016-02-03
中文关键词:  纳米晶合金  元素掺杂  晶体结构  原子占位  内禀矫顽力
基金项目:国家自然科学基金资助(项目号51371012, 51425101)
中文摘要:
      首先制备出纳米晶组织的Sm5Co19Hf0.4合金和Sm5Co19Hf0.4CNTs0.4合金,对其显微组织、晶体结构和磁性能等进行了系统表征分析。结果表明:Hf元素和碳纳米管CNTs的混合添加不引起Sm5Co19合金Ce5Co19型结构发生相分解,且使纳米晶组织中晶粒细小,晶粒尺寸均匀分布。能谱分析表明,添加的CNTs进入纳米晶Sm5Co19Hf0.4CNTs0.4合金的晶界区域,产生晶界钉扎作用,显著提高纳米晶Sm5Co19合金的矫顽力。晶体结构精修表明,Hf元素进入纳米晶Sm5Co19合金晶胞结构的Sm空位,导致晶格参数a、b、c均减小,而轴比c/a增加,使Hf掺杂的纳米晶合金的磁晶各向异性增大,具有提高纳米晶合金的矫顽力的作用。本文研究结果对设计制备具有高磁晶各向异性、高内禀矫顽力的Sm-Co基合金具有明确指导意义。
Effect of Alloy Structure and the Magnetic Mix Doping Hf Elements and CNTs on Nanocrystalline Sm5Co19 Alloy
英文关键词:nanocrystalline  element doping  crystal structure  atom occupancy  intrinsic coercivity
英文摘要:
      In this study, permanent magnetic nanocrystalline Sm5Co19Hf0.4 alloy and Sm5Co19Hf0. 4CNTs0. 4 alloy with high room-temperature coercivity were produced. The microstructure, crystal structure and magnetic were studied. The results show that the Hf elements and CNTs mixed added did not lead to phase decomposition of Ce5Co19 type structure, meanwhile the microstructure possess fine grain size and uniform distribution. Energy Dispersive X-ray Spectrometry (EDX) analysis confirmed that CNTs move into grain boundaries of the nanocrystalline Sm5Co19Hf0.4CNTs0.4alloy, which can improve the coercivity of the nanocrystalline Sm5Co19 alloy for the grain boundary pinning effect. Rietyeld refinement showed that Hf comes into the Sm vacancy decreasing the lattice parameters and increasing the axial ratio c/a , which furtherly enhance the magnetocrystalline anisotropy , thus strengthen the coercivity of nanocrystalline alloy. In this paper, the results of the study can promote the design of Sm-Co alloy with high magnetocrystalline anisotropy and intrinsic coercivity.
作者单位E-mail
王东鑫 北京工业大学材料科学与工程学院新型功能材料教育部重点实验室 wdx@emails.bjut.edu.cn 
乔印凯 北京工业大学材料科学与工程学院新型功能材料教育部重点实验室  
刘东 北京工业大学材料科学与工程学院新型功能材料教育部重点实验室  
华刚 北京工业大学材料科学与工程学院新型功能材料教育部重点实验室  
王海滨 北京工业大学材料科学与工程学院新型功能材料教育部重点实验室  
刘雪梅 北京工业大学材料科学与工程学院新型功能材料教育部重点实验室  
宋晓艳 北京工业大学材料科学与工程学院新型功能材料教育部重点实验室 xysong@bjut.edu.cn 
摘要点击次数: 38
全文下载次数: 10
查看全文  查看/发表评论  下载PDF阅读器
关闭