+高级检索
低Re镍基单晶高温合金平衡相析出行为的热力学模拟计算
DOI:
作者:
作者单位:

清华大学材料学院先进成形制造教育部重点实验室,中国航发沈阳黎明航空发动机 集团 有限责任公司,清华大学材料学院先进成形制造教育部重点实验室,清华大学材料学院先进成形制造教育部重点实验室

作者简介:

通讯作者:

中图分类号:

TG111.5

基金项目:

国家自然科学(51374137和51171089);国家科技重大专项(2012ZX04012-011);国家重点基础研发项目(2011CB706801)


Thermodynamic Simulation Calculation on Precipitation Behavior of Equilibrium Phases in a Low Re-bearing Nickel-based Single Crystal Superalloy
Author:
Affiliation:

Key Laboratory for Advanced Materials Processing Technology,Ministry of Education,School of Materials Science and Engineering,Tsinghua University,Aero Engine Corporation of China AECC Shenyang Liming Aero-Engine Group Corporation Ltd,Key Laboratory for Advanced Materials Processing Technology,Ministry of Education,School of Materials Science and Engineering,Tsinghua University,Key Laboratory for Advanced Materials Processing Technology,Ministry of Education,School of Materials Science and Engineering,Tsinghua University

Fund Project:

  • 摘要
  • |
  • 图/表
  • |
  • 访问统计
  • |
  • 参考文献
  • |
  • 相似文献
  • |
  • 引证文献
  • |
  • 资源附件
  • |
  • 文章评论
    摘要:

    基于Pandat热力学计算软件及PanNi数据库, 采用热力学相平衡计算方法, 研究了合金成分对低铼DD6合金平衡相析出行为的影响。结果表明: DD6合金平衡相主要为γ相、γ′相、μ相及碳化物MC和M23C6, 计算结果与实验结果吻合。γ′相析出量主要由Al、Ta和Nb含量控制, 随Al、Ta和Nb含量增加, γ′相析出量显著增加, 固溶温度明显升高, 液相初凝与终凝温度逐渐降低。C含量决定MC和M23C6的析出量, MC和M23C6析出量随C含量增加而增大。μ相析出主要受Re、W、Mo和Cr的影响, 随Re、W、Mo和Cr含量增加, μ相开始析出温度显著升高, 析出温度范围明显变宽, 最大析出量明显增大。

    Abstract:

    Based on thermodynamic calculation Pandat software and PanNi database, thermodynamic phase equilibrium calculation method was employed to investigate the effect of alloying composition on precipitation behavior of equilibrium phases in a low Re-containing nickel-based single crystal superalloy DD6. Results indicate that the equilibrium phases consist of γ, γ′, μ, MC and M23C6, and the calculated results are in excellent agreement with the experimental results. The Al, Ta and Nb content mainly control the mass fraction of γ′ precipitates. With increase of Al, Ta and Nb content, the mass fraction of γ′ precipitates is significantly enhanced, the solution temperature of γ′ precipitates is obviously increased, and the liquid starting and finishing solidification temperature is gradually decreased. The C content determines the precipitation amount of MC and M23C6. Increment of C content results in more precipitation of carbides. The precipitation of μ phase is predominantly influenced by Re, W, Mo and Cr. With the increase of Re, W, Mo and Cr content, the initial precipitation temperature of μ phase is significantly enhanced, the maximum precipitation amount of μ phase is obviously increased, and the precipitation temperature range of μ phase is markedly extended.

    参考文献
    相似文献
    引证文献
引用本文

苏香林,孙长波,许庆彦,柳百成.低Re镍基单晶高温合金平衡相析出行为的热力学模拟计算[J].稀有金属材料与工程,2017,46(12):3699~3714.[Su Xianglin, Sun Changbo, Xu Qingyan, Liu Baicheng. Thermodynamic Simulation Calculation on Precipitation Behavior of Equilibrium Phases in a Low Re-bearing Nickel-based Single Crystal Superalloy[J]. Rare Metal Materials and Engineering,2017,46(12):3699~3714.]
DOI:[doi]

复制
文章指标
  • 点击次数:
  • 下载次数:
  • HTML阅读次数:
  • 引用次数:
历史
  • 收稿日期:2017-03-31
  • 最后修改日期:2017-09-28
  • 录用日期:2017-10-10
  • 在线发布日期: 2018-01-04
  • 出版日期: