TiZrNiCu/Ti60润湿性及与TiBw-TC4钎焊研究
DOI:
作者:
作者单位:

1.哈尔滨工业大学先进焊接与连接国家重点实验室;2.哈尔滨工业大学(威海)山东省特种焊接技术重点实验室;3.哈尔滨工业大学

作者简介:

通讯作者:

中图分类号:

基金项目:

国家自然科学基金项目(面上项目,重点项目,重大项目)


Wettability of TiZrNiCu-B/Ti60 system and its brazing to TiBw-TC4 composite
Author:
Affiliation:

1.State Key Laboratory of Advanced Welding and Joining,Harbin Institute of Technology;2.Shandong Provincial Key Lab of Special Welding Technology,Harbin Institute of Technology at Weihai;3.Department of Chemistry,Harbin Institute of Technology

Fund Project:

The National Natural Science Foundation of China (General Program, Key Program, Major Research Plan)

  • 摘要
  • |
  • 图/表
  • |
  • 访问统计
  • |
  • 参考文献
  • |
  • 相似文献
  • |
  • 引证文献
  • |
  • 资源附件
  • |
  • 文章评论
    摘要:

    本文采用座滴法在真空下系统研究了硼含量对TiZrNiCu/Ti60润湿性的影响,且在940°C保温10分钟条件下实现了与的钎焊。通过SEM、XRD以及剪切实验研究了界面显微组织及剪切力学性能。添加B元素可以与Ti原位合成TiBw,从而细化界面的显微组织。当B含量为0.3 wt %时,TiBw-TC4 /TiZrNiCu-B/Ti60接头的最大剪切强度为177 MPa,比无B含量的接头强度高65%。然而,过量的B含量使TiZrNiCu-B在Ti60合金基体上产生大量的TiBw,导致润湿性恶化,在钎焊接头形成微孔和未焊合区域,从而使剪切强度下降。

    Abstract:

    In this work, the connection between the boron content and the wettability of TiZrNiCu/Ti60 system was studied by sessile drop method of elevating and maintaining isothermal process under vacuum, and TiBw-TC4 composite was successfully brazed to Ti60 alloy using TiZrNiCu-B filler alloy with brazing temperature of 940 °C for 10 min. The contact angle of TiZrNiCu/Ti60 alloy substrate and the corresponding interfacial microstructure, the interfacial microstructures and shear fractures of brazed joints were studied using SEM, EDS and XRD, and the influence of B content on interfacial microstructure and joining properties was also investigated in detail. Added B element can react with Ti to in-situ synthesizing TiB whiskers (TiBw), which resulted in a relative refinement of microstructure. And the maximum shear strength of TiBw-TC4/TiZrNiCu-B/Ti60 joint was 177 MPa when the content of B is 0.3 wt.%, which was 65% higher than the joints brazed without B content. However, the excessive B content worsened the wetting behavior of TiZrNiCu-B on Ti60 alloy substrate, resulted in the microvoids and disconnected area in the brazed joint, and the shear strength decreased inevitably.

    参考文献
    相似文献
    引证文献
引用本文

胡胜鹏,陈祖斌,雷玉珍,宋晓国,康佳睿,曹健,唐冬雁. TiZrNiCu/Ti60润湿性及与TiBw-TC4钎焊研究[J].稀有金属材料与工程,2019,48(3):701~710.[S. P. Hu, Z. B. Chen, Y. Z. Lei, X. G. Song, J. R. Kang, J. Cao, D. Y. Tang. Wettability of TiZrNiCu-B/Ti60 system and its brazing to TiBw-TC4 composite[J]. Rare Metal Materials and Engineering,2019,48(3):701~710.]
DOI:[doi]

复制
文章指标
  • 点击次数:
  • 下载次数:
  • HTML阅读次数:
  • 引用次数:
历史
  • 收稿日期:2017-10-09
  • 最后修改日期:2017-10-27
  • 录用日期:2017-11-08
  • 在线发布日期: 2019-04-10
  • 出版日期: