侯可可,黄娇,姚美意,孙蓉蓉,龙冲生,张金龙,周邦新.Stress and Defect Characteristics in Oxide Films and Corrosion Resistance of Zr-1Nb Alloy[J].稀有金属材料与工程,2019,48(5):1440~1446.[Hou Keke,Huang Jiao,YAO Meiyi,Sun Rongrong,Long Chongsheng,Zhang Jinlong,Zhou Bangxin.Stress and Defect Characteristics in Oxide Films and Corrosion Resistance of Zr-1Nb Alloy[J].Rare Metal Materials and Engineering,2019,48(5):1440~1446.]
Stress and Defect Characteristics in Oxide Films and Corrosion Resistance of Zr-1Nb Alloy
投稿时间:2017-12-23  修订日期:2018-01-11
中文关键词:  Zirconium alloys  Corrosion  Ion migration method  Defects  Stress
基金项目:国家自然科学基金项目
中文摘要:
      Two approaches to testing corrosion in autoclave with different time intervals for heating and cooling were carried out to investigate the corrosion resistance of Zr-1Nb alloy in the 0.01 mol/L LiOH aqueous solution at 360 °C/18.6 MPa, the stress, and defect density in the oxide film. The stress and defect density in oxide film were measured by a curl method and the Ion Migration Method (IMM), respectively. Results showed that the stress level and defect density in the oxide film in the shorter interval corrosion tests were lower than that in the longer interval corrosion tests at the initial stage of corrosion with the weight gain less than 34.37 mg/dm2. The corrosion resistance in the subsequent stages of corrosion was better in the shorter interval corrosion tests. It indicates that at the initial stage of corrosion the weight gain shows no obvious difference between the two approaches of corrosion tests in autoclave under different time intervals for heating and cooling. However, the stress level and defect density in the oxide film exhibit noticeable differences, which leads to two distinct microstructural evolution rates of the oxide film. The distinct microstructural evolution rates cause different corrosion resistance in the subsequent corrosion stages.
Stress and Defect Characteristics in Oxide Films and Corrosion Resistance of Zr-1Nb Alloy
英文关键词:Zirconium alloys  Corrosion  Ion migration method  Defects  Stress
英文摘要:
      Two approaches to testing corrosion in autoclave with different time intervals for heating and cooling were carried out to investigate the corrosion resistance of Zr-1Nb alloy in the 0.01 mol/L LiOH aqueous solution at 360 °C/18.6 MPa, the stress, and defect density in the oxide film. The stress and defect density in oxide film were measured by a curl method and the Ion Migration Method (IMM), respectively. Results showed that the stress level and defect density in the oxide film in the shorter interval corrosion tests were lower than that in the longer interval corrosion tests at the initial stage of corrosion with the weight gain less than 34.37 mg/dm2. The corrosion resistance in the subsequent stages of corrosion was better in the shorter interval corrosion tests. It indicates that at the initial stage of corrosion the weight gain shows no obvious difference between the two approaches of corrosion tests in autoclave under different time intervals for heating and cooling. However, the stress level and defect density in the oxide film exhibit noticeable differences, which leads to two distinct microstructural evolution rates of the oxide film. The distinct microstructural evolution rates cause different corrosion resistance in the subsequent corrosion stages.
作者单位E-mail
侯可可 上海大学材料研究所 hkk0510@163.com 
黄娇 上海大学材料研究所  
姚美意 上海大学材料研究所 yaomeiyi@shu.edu.cn 
孙蓉蓉 上海大学材料研究所  
龙冲生 中国核动力研究设计院  
张金龙 上海大学材料研究所  
周邦新 上海大学材料研究所  
摘要点击次数: 163
全文下载次数: 91
查看全文  查看/发表评论  
关闭