热处理对哈氏合金X焊接接头组织与性能的影响
DOI:
作者:
作者单位:

1.中国民航大学 天津市民用航空器适航与维修重点实验室 天津;2.中国民航大学 理学院 天津

作者简介:

通讯作者:

中图分类号:

基金项目:

民航局重大专项(项目号MHRD20160106);大学生创新创业项目(项目号IECAUC2017038)


Effect of Heat Treatment on Microstructure and Properties of Hastelloy X Welded Joints
Author:
Affiliation:

Civil Aviation University of China,Tianjin Key Laboratory of Civil Aircraft Airworthiness and Maintenance,Tianjin, College of science Civil Aviation University of China Tianjin

Fund Project:

  • 摘要
  • |
  • 图/表
  • |
  • 访问统计
  • |
  • 参考文献
  • |
  • 相似文献
  • |
  • 引证文献
  • |
  • 资源附件
  • |
  • 文章评论
    摘要:

    本实验研究不同热处理工艺对哈氏合金X焊接接头组织和力学性能的影响,分析焊后热处理对哈氏合金X焊接接头性能的影响规律。结果表明:焊缝中心区域组织主要以等轴晶为主,熔合区以枝晶为主。经1050℃热处理的焊缝未析出二次相,经1100℃处理的焊缝在晶界处与晶粒内析出大量二次相,经1150℃处理的焊缝析出物发生重溶。经1150℃热处理工艺后接头抗拉强度最高达773.49 MPa;经1100℃处理的焊接接头断裂形式为沿晶脆性断裂,其他焊缝接头的断裂形式为韧性断裂。

    Abstract:

    Effect of different heat treatment processes on the microstructure and mechanical properties of TIG welded Hastelloy X welded joints was studied by SEM and EDS. The results showed that the central area of the weld was mainly composed of fine equiaxed grains, and the fusion zone was dominated by dendrites. The secondary phase was not precipitated in the weld joints heat treated at 1050°C, and a large number of secondary phases were precipitated in the grains at the grain boundary at 1100°C. The secondary phase at 1150°C were partly re-dissolved. The tensile strength of joint reaches up to 773.49 MPa after heat treatment at 1150°C. The joint treated at 1100°C was intergranular fractures, the rest were ductile fractures.

    参考文献
    相似文献
    引证文献
引用本文

孙宇博,靳朋礼 马锦晖 和晶 崔景豪 周可人 崔梦茜.热处理对哈氏合金X焊接接头组织与性能的影响[J].稀有金属材料与工程,2019,48(9):3029~3034.[Sun yubo, jin pengli. Effect of Heat Treatment on Microstructure and Properties of Hastelloy X Welded Joints[J]. Rare Metal Materials and Engineering,2019,48(9):3029~3034.]
DOI:[doi]

复制
文章指标
  • 点击次数:
  • 下载次数:
  • HTML阅读次数:
  • 引用次数:
历史
  • 收稿日期:2018-04-06
  • 最后修改日期:2018-05-14
  • 录用日期:2018-06-15
  • 在线发布日期: 2019-10-09
  • 出版日期: