Effect of pre-aging treatment on the stability of Al-5.2Mg-0.45Cu-2.0Zn alloy sheet at room temperature
Author:
Affiliation:

State Key Laboratory of Advanced Metals and Materials,University of Science and Technology Beijing

Fund Project:

  • 摘要
  • |
  • 图/表
  • |
  • 访问统计
  • |
  • 参考文献
  • |
  • 相似文献
  • |
  • 引证文献
  • |
  • 资源附件
  • |
  • 文章评论
    摘要:

    本文详细研究了预时效对Al-5.2Mg-0.45Cu-2.0Zn合金时效析出行为的影响。预时效不仅提高了合金的室温稳定性,避免了合金烤漆软化,同时提高了合金的烤漆时效响应速度。合金经T4处理后,再峰时效处理后的组织包括粗大的T-Mg32(AlZn)49相以及针状的S-Al2MgCu相。然而合金经T4P处理后,再峰时效处理的组织只含有细小而高密度的T-Mg32(AlZn)49相而不包括S-Al2MgCu相。自然时效后不稳定的原子团簇在180℃时效后会回溶到基体中, 从而抑制了合金的时效析出强化。而预时效后生成的稳定的原子团簇会成为180℃时效的形核点,显著提高了合金的时效响应速度。

    Abstract:

    In this research, pre-aging treatment has been performed on our newly developed Al-5.2Mg-0.45Cu-2.0Zn alloy. Results show that pre-aging treatment not only improves the stability of the alloy sheet at room temperature, which avoids the paint-baking softening, but also enhances the age hardening response during subsequent artificial aging at 180℃. The microstructure of the T4 sample in peak aged condition consists of coarse lath-like T-Mg32(AlZn)49 phase and needle-like S-Al2MgCu phase. However, the microstructure of the T4P sample in peak aged condition only consists of high density of finer and equiaxed T phase with the S phase disappeared. Unstable clusters formed during natural aging dissolve when imposed on 180℃, which retards the precipitation process of the alloy. Stable clusters formed during pre-aging treatment serves as the nucleis of the T phase during aging at 180℃, which enhances the age hardening response of the alloy.

    参考文献
    相似文献
    引证文献
引用本文

曹城,张迪,庄林忠,张济山.预时效对Al-5.2Mg-0.45Cu-2.0Zn合金室温稳定性的影响[J].稀有金属材料与工程,2020,49(4):1166~1170.[Cheng Cao, Di Zhang, Linzhong Zhuang, Jishan Zhang. Effect of pre-aging treatment on the stability of Al-5.2Mg-0.45Cu-2.0Zn alloy sheet at room temperature[J]. Rare Metal Materials and Engineering,2020,49(4):1166~1170.]
DOI:[doi]

复制
文章指标
  • 点击次数:
  • 下载次数:
  • HTML阅读次数:
  • 引用次数:
历史
  • 收稿日期:2018-04-12
  • 最后修改日期:2020-03-25
  • 录用日期:2019-12-04
  • 在线发布日期: 2020-05-07
  • 出版日期: