CP-Ti在含氟离子硝酸中表面附着物形成研究
DOI:
作者:
作者单位:

1.太原理工大学新材料工程技术研究中心;2.西北有色金属研究院

作者简介:

通讯作者:

中图分类号:

基金项目:

陕西省重点研发计划项目(2017ZDXM-GY-044)


Formation mechanism of surface attachment of CP-Ti in nitric acid containing fluoride ions
Author:
Affiliation:

Research Center of Advanced Materials Science and Technology, Taiyuan University of Technology

Fund Project:

  • 摘要
  • |
  • 图/表
  • |
  • 访问统计
  • |
  • 参考文献
  • |
  • 相似文献
  • |
  • 引证文献
  • |
  • 资源附件
  • |
  • 文章评论
    摘要:

    钛具有优良的耐蚀性能,可长期工作在高浓度的沸腾硝酸介质中,是商业后处理较为理想的设备用材。本文采用SEM,EDS,XRD,XPS等表征手段对CP-Ti在含氟离子硝酸中试样表面出现的白色附着物进行分析,并解释其形成机理。结果表明:氟离子浓度在50 ppm以下时,CP-Ti腐蚀速率呈现由大到小并趋于稳定的规律;氟离子浓度在50 ppm及以上时,腐蚀速率呈现由大到小再变大的“v”型规律。试样表面的白色附着物的物相为TiO<sub>2</sub>,其形成机理为:先是试样表面多孔膜的形成;其次是TiO<sub>2</sub>以多孔膜上的孔为基点进行生长、脱落。

    Abstract:

    <sub></sub><sub>:</sub><sub>Titanium</sub><sub> has excellent corrosion resistance and can be used for long-term operation in boil</sub><sub>ing high concentration </sub><sub>nitric</sub><sub> acid medium. It is</sub><sub>an ideal</sub><sub> material for </sub><sub>re</sub><sub>processing equipment</sub><sub>. In this paper, SEM, EDS, XRD</sub><sub> and </sub><sub>XPS characterization methods were used to</sub><sub>analyze</sub><sub>the white attachment of the surface of </sub><sub>CP-</sub><sub>Ti</sub><sub>in</sub><sub> nitric acid</sub><sub> with </sub><sub>fluorine ion and explain its formation mechanism. The results show that when the concentration of fluorine ions is below 50 ppm, the corrosion rate of CP-</sub><sub>Ti</sub><sub> appears from large to small and tends to be stable. When the concentration of fluorine ions is 50 ppm and above, the corrosion rate appears from large to small and tends to large presents the "V" pattern. The phase of the white attachment of the surface of </sub><sub>CP-</sub><sub>Ti</sub><sub> is TiO</sub><sub>2</sub><sub>. </sub><sub>The formation mechanism of the attachment is divided into two steps</sub><sub>:</sub><sub>first</sub><sub>ly</sub><sub>, the formation of porous </sub><sub>film</sub><sub> on the surface of the CP-</sub><sub>Ti</sub><sub>; secondly,</sub> <sub>The</sub><sub> TiO</sub><sub>2</sub><sub> is gro</sub><sub>wn on the pore of porous </sub><sub>film</sub><sub> as the base point</sub><sub> and</sub><sub> then</sub><sub>shedding.</sub>

    参考文献
    相似文献
    引证文献
引用本文

徐建平,苏航标,郭荻子,赵永庆,许并社,周廉. CP-Ti在含氟离子硝酸中表面附着物形成研究[J].稀有金属材料与工程,2019,48(11):3615~3620.[xujianping, suhangbiao, guodizi, zhaoyongqing, xubingshe, zhoulian. Formation mechanism of surface attachment of CP-Ti in nitric acid containing fluoride ions[J]. Rare Metal Materials and Engineering,2019,48(11):3615~3620.]
DOI:[doi]

复制
文章指标
  • 点击次数:
  • 下载次数:
  • HTML阅读次数:
  • 引用次数:
历史
  • 收稿日期:2018-07-30
  • 最后修改日期:2018-08-23
  • 录用日期:2018-08-24
  • 在线发布日期: 2019-12-10
  • 出版日期: