基底表面质量对ZK60镁合金镀镍层性能的影响
DOI:
作者:
作者单位:

1.西北工业大学凝固技术国家重点实验室;2.西安空间无线电技术研究所

作者简介:

通讯作者:

中图分类号:

基金项目:

国家重点研发计划(2018YFB1106800);国家自然科学基金资助(51420105005,51771152);宁夏“十三五”重大科技项目(2018BCE01001)


Effect of Substrate Surface Quality on Nickel Plating Property of ZK60 Magnesium Alloy
Author:
Affiliation:

1.State Key Laboratory of Solidification Processing,Northwestern Polytechnical University,Xi’an;2.Xi’an Institute of Space Radio Technology,Xi’an

Fund Project:

  • 摘要
  • |
  • 图/表
  • |
  • 访问统计
  • |
  • 参考文献
  • |
  • 相似文献
  • |
  • 引证文献
  • |
  • 资源附件
  • |
  • 文章评论
    摘要:

    镁合金表面镀镍被广泛运用于镁合金工件防腐,而镀层的起泡和脱落严重影响工件的使用寿命。本文以ZK60镁合金为对象,研究了不同工件基底表面质量对镀镍层的影响机制。研究表明:基底表面存在的划痕和点蚀坑会显著降低镀镍层质量,引起镀层的起泡和脱落。基底表面的划痕会被保留到镀镍层中,引发镀层变薄,应力集中等问题,增加镀层开裂的几率。点蚀坑中的杂质与镁基底有不同的电化学特性,会导致镀层减薄和结合不牢。因此,提高镁合金工件基底表面光洁度、清除基底表面点蚀坑是提高镁合金镀镍层性能的必要措施。

    Abstract:

    Nickel plating on the surface of magnesium alloy is widely used in the anti-corrosion of magnesium alloy workpiece, but blistering and peeling from nickel plating will seriously affect service life of the workpiece. In this paper, effects of the different substrate surfaces on nickel plating properties of ZK60 magnesium alloy were studied. The results showed that the surface scratch and corrosive pitting significantly reduced the coating quality and caused blistering and peeling from nickel plating. The surface scratch of the substrate was retained under the nickel plating layer, which made the coating thinner, and caused stress concentration in the coating, and increased the probability of coating cracking. Differences in electrochemical properties between impurities in pitting pits and magnesium substrate led to thinning of the coating and weakened the adhesion of the coating. Therefore, good substrate surface finish and no substrate surface corrosive pitting are the guarantee of high quality nickel plating of magnesium alloy workpiece.

    参考文献
    相似文献
    引证文献
引用本文

郑循威,杨光昱,黄光孙,田普科,罗时峰,介万奇.基底表面质量对ZK60镁合金镀镍层性能的影响[J].稀有金属材料与工程,2020,49(6):2161~2167.[Zheng Xunwei, Yang Guangyu, Huang Guangsun, Tian Puke, Luo Shifeng, Jie Wanqi. Effect of Substrate Surface Quality on Nickel Plating Property of ZK60 Magnesium Alloy[J]. Rare Metal Materials and Engineering,2020,49(6):2161~2167.]
DOI:[doi]

复制
文章指标
  • 点击次数:
  • 下载次数:
  • HTML阅读次数:
  • 引用次数:
历史
  • 收稿日期:2019-04-15
  • 最后修改日期:2019-06-21
  • 录用日期:2019-07-02
  • 在线发布日期: 2020-07-09
  • 出版日期: