曹廷,李小强,李京懋,黄阳,宋涛,屈盛官,梁良.超细氮化硼多孔纤维对WC-ZrO2复合材料力学性能的改善[J].稀有金属材料与工程,2021,50(3):802~806.[Ting Cao,Xiaoqiang Li,Jingmao Li,Yang Huang,Tao Song,Shengguan Qu,Liang Liang.Improvements of mechanical properties of WC-ZrO2 composites with addition of ultrafine porous boron nitride nanofiber[J].Rare Metal Materials and Engineering,2021,50(3):802~806.]
超细氮化硼多孔纤维对WC-ZrO2复合材料力学性能的改善
投稿时间:2020-02-27  修订日期:2020-07-01
中文关键词:  多孔纤维  碳化钨  氧化锆  杨氏模量
基金项目:the Natural Science Foundation of China (No.51474108, 51575193, and 51402086), the Hundred Talents Program of Hebei Province (E2014100011), the Key Project of Guangdong Natural Science Foundation (No.2018B030311051), and the Heyuan Science and Technology Project (heke2018009).
中文摘要:
      本研究采用放电等离子烧结方法首次制备了超细氮化硼多孔纤维改善的WC-ZrO2复合材料。在添加了超细氮化硼多孔纤维之后,样品的硬度和断裂韧性同时获得了提升。而个别成分样品的杨氏模量则突破了复合材料混合法则的局限,高达692GPa,接近纯WC的杨氏模量 700GPa。
Improvements of mechanical properties of WC-ZrO2 composites with addition of ultrafine porous boron nitride nanofiber
英文关键词:porous nanofibers  WC  ZrO2  Young’s modulus.
英文摘要:
      In this study, using spark plasma sintering, an ultrafine porous boron nitride nanofiber-improved WC-ZrO2 composite was prepared. The obtained composites displayed superior properties in terms of hardness and fracture toughness. In particular, the Young’s modulus value increased but did not follow the rule of mixtures for most of ceramics-based composites (up to 692 GPa, close to 700 GPa of pure WC).
作者单位E-mail
曹廷 华南理工大学国家金属材料近净成形工程技术研究中心 ctct_13@163.com 
李小强 华南理工大学国家金属材料近净成形工程技术研究中心 lixq@scut.edu.cn 
李京懋 华南理工大学国家金属材料近净成形工程技术研究中心  
黄阳 河北工业大学材料科学与工程学院  
宋涛 河北工业大学材料科学与工程学院  
屈盛官 华南理工大学国家金属材料近净成形工程技术研究中心  
梁良 华南理工大学国家金属材料近净成形工程技术研究中心  
摘要点击次数: 56
全文下载次数: 41
查看全文  查看/发表评论  
关闭