辅助电流对Cu/Al大功率超声波焊接的影响
作者:
作者单位:

1.长江大学机械工程学院;2.天津大学材料科学与工程学院;3.北京航空航天大学机械工程及自动化学院;4.北京理工大学机电学院

作者简介:

通讯作者:

中图分类号:

TG456.9

基金项目:

国家自然科学基金资助(项目号51605103); 湖北省重点研发计划项目(项目号2020BAB055)


Effect of Assisted Current on High-Power Cu/Al Ultrasonic Welding
Author:
Affiliation:

1.School of Mechanical Engineering,Yangtze University;2.School of Mechanical Engineering and Automation,Beihang University

Fund Project:

The Natural Science Foundation of China;Key Scientific Research Foundation by Science and Technology Department of Hubei Province

  • 摘要
  • |
  • 图/表
  • |
  • 访问统计
  • |
  • 参考文献
  • |
  • 相似文献
  • |
  • 引证文献
  • |
  • 资源附件
  • |
  • 文章评论
    摘要:

    为获得更高质量的Cu/Al异质金属接头,开展了Cu/Al电流辅助大功率超声波焊接工艺试验,研究了辅助电流对Cu/Al超声波焊接的界面温度、材料塑性流动、界面中间相分布及接头力学性能的影响。结果表明,复合焊件成型良好,其接头抗拉剪力为3030 N,接头的断裂模式为韧性-脆性复合断裂。在同样的焊接时间0.2 s内,随着电流的增大,Cu/Al界面温度增加,金属塑性流动以及界面扩散也随之增强,这说明辅助电流能明显促进界面冶金;相比长时间0.4 s的超声波焊接,辅助电流能在保证界面温度、材料塑性变形的前提下,能明显减薄了界面IMC层的厚度,这是电流增强Cu/Al接头的主要物理机制。研究结果为优化Cu/Al复合焊接头强度提供了参考。

    Abstract:

    In order to obtain reliable Cu/Al dissimilar joints, current assisted Cu/Al high-power ultrasonic welding was proposed. The effects of current on the temperature rise, plastic flow, intermetallic compound (IMC) growth, and mechanical properties of the joints in Cu/Al ultrasonic welding were investigated. The results show that the obtained hybrid welded joint is well bonded, the tensile-shear force of the hybrid welding joint is 3030 N, and the fracture mode of the hybrid welding joint is ductile-brittle composite fracture. At the same welding time of 0.2 s, with the increase of the current, the peak temperature of the Cu/Al interface increases, and the metal plastic flow and diffusion at the interface also increase. This indicates that the assisted current can significantly enhance the interfacial metallurgy; compared with the single ultrasonic welding at welding time of 0.4 s, the assisted current can meet the welding formation requirements of interface temperature and material plastic deformation, but reduce the thickness of the interface IMC layer. This is the primary reason for the enhanced Cu/Al joint by assisted current. The results provide guidance for optimizing the strength of Cu/Al current assisted ultrasonic welded joints.

    参考文献
    相似文献
    引证文献
引用本文

李 欢,张长鑫,敖三三,曾才有,周 亢.辅助电流对Cu/Al大功率超声波焊接的影响[J].稀有金属材料与工程,2022,51(12):4624~4631.[LI Huan, ZHANG Changxin, AO Sansan, ZENG Caiyou, ZHOU Kang. Effect of Assisted Current on High-Power Cu/Al Ultrasonic Welding[J]. Rare Metal Materials and Engineering,2022,51(12):4624~4631.]
DOI:10.12442/j. issn.1002-185X.20220275

复制
文章指标
  • 点击次数:
  • 下载次数:
  • HTML阅读次数:
  • 引用次数:
历史
  • 收稿日期:2022-04-04
  • 最后修改日期:2022-06-20
  • 录用日期:2022-07-12
  • 在线发布日期: 2023-01-19
  • 出版日期: 2022-12-30