<bold>Yb</bold>元素对<bold>BAg30</bold>硬钎料及焊点组织与性能的影响

doi:10.12442/j.issn.1002-185X.E20210532

首页 > 过刊浏览>2022年第51卷第7期 >2344-2348. DOI:10.12442/j.issn.1002-185X.E20210532

Yb元素对BAg30硬钎料及焊点组织与性能的影响
DOI:
                        10.12442/j.issn.1002-185X.E20210532
                    
作者:
                        
                        
                    
作者单位:1.郑州机械研究所有限公司，河南 郑州 450001;2.江苏师范大学 机电工程学院，江苏 徐州 221116
作者简介:
通讯作者:
中图分类号:
基金项目:Major State Research Development Program of China (2019YFF0217400); the Central Plains Science and Technology Innovation Leading Talents Program (ZYQR20180030).

Influences of Ytterbium on Microstructure and Properties of BAg30 Filler Metals and Brazed Joints

Author:

Affiliation:

1.Zhengzhou Research Institute of Mechanical Engineering Co., Ltd, Zhengzhou 450001, China;2.School of Mechatronic Engineering, Jiangsu Normal University, Xuzhou 221116, China

Fund Project:

Major State Research Development Program of China (2019YFF0217400); Central Plains Science and Technology Innovation Leading Talents Program (ZYQR20180030)

摘要

图/表

访问统计

参考文献

相似文献

引证文献

资源附件

文章评论

摘要:

研究了Yb元素对Ag30-Cu-Zn-Sn（BAg30）钎料热性能、润湿性和微观组织的影响，分析了焊点的剪切强度和断口形貌，优化了钎料组分。结果表明，BAg30钎料添加1%（质量分数，下同）Yb后可以显著降低钎料液相线-固相线差值，促进钎料在钢基板表面的润湿性，细化微观组织。然而，当Yb添加量超过1%后，过量的Yb元素会降低钎料的性能，粗化微观组织。通过焊点剪切测试，BAg30-1% Yb钎料的焊点抗剪切强度和断裂形貌表现出明显的优越性，抗剪切强度相较于BAg30钎料焊点明显提高，断口形貌出现均匀细小的韧窝，表现为韧性断裂机制。

Abstract:

The effects of ytterbium (Yb) on the thermal behavior, wettability, and microstructures of Ag30-Cu-Zn-Sn (BAg30) filler metals were investigated. The shear strength and fracture morphology of brazed joints were analyzed to optimize the filler composition. Results reveal that the addition of 1wt% Yb in BAg30 filler metal can significantly decrease the temperature difference between solidus temperature and liquidus temperature, improve the wettability of filler on the steel substrate, and refine the microstructures. However, the excessive addition of Yb (more than 1wt%) can degrade the properties and coarsen the microstructure. According to the shear strength tests, the BAg30-1wt% Yb brazed joint shows obvious superiority in shear strength and fracture morphology: its shear strength is higher than that of the original BAg30 brazed joint, and the fracture mechanism is ductile fracture, presenting the homogeneous and fine dimples.

参考文献

相似文献

引证文献

引用本文

张亮,钟素娟,董宏伟,王蒙,龙伟民.Yb元素对BAg30硬钎料及焊点组织与性能的影响[J].稀有金属材料与工程,2022,51(7):2344~2348.[Zhang Liang, Zhong Sujuan, Dong Hongwei, Wang Meng, Long Weimin. Influences of Ytterbium on Microstructure and Properties of BAg30 Filler Metals and Brazed Joints[J]. Rare Metal Materials and Engineering,2022,51(7):2344~2348.]
DOI：10.12442/j. issn.1002-185X. E20210532

复制

文章指标

点击次数:
下载次数:
HTML阅读次数:
引用次数:

历史

收稿日期:2021-06-22
最后修改日期:2021-08-18
录用日期:2021-09-01
在线发布日期: 2022-08-03
出版日期: 2022-07-27

首页

期刊简介

学术影响

编委会

投稿指南

常见问答

联系我们

English

引用本文

文章指标

历史