沈永华,张玉平,程焕武,王扬卫,王迎春,李硕.多孔SiC陶瓷/Zr基非晶合金复合材料动态压缩性能研究[J].稀有金属材料与工程,2020,49(2):737~743.[SHEN Yonghua,Zhang Yuping,CHENG Huanwu,WANG Yangwei,WANG Yingchun,and LI Shuo.The research on the Dynamic Compressive Properties of Porous SiC Ceramic/ Zr-Base Amorphous Composites[J].Rare Metal Materials and Engineering,2020,49(2):737~743.]
多孔SiC陶瓷/Zr基非晶合金复合材料动态压缩性能研究
投稿时间:2019-03-12  修订日期:2019-12-10
中文关键词:  多孔SiC陶瓷  非晶合金  复合材料  动态压缩  解理台阶  脉状花样
基金项目:
中文摘要:
      通过压力-浸渗法制备多孔SiC陶瓷/Zr基非晶合金复合材料。利用分离式霍普金森压杆装置(SHPB)、S-4800场发射扫描电镜等测试分析手段,探究复合材料制备保温时间和多孔碳化硅性能对多孔SiC陶瓷/Zr基非晶合金复合材料动态压缩性能的影响,并揭示了其变形机制。结果表明:保温时间和多孔碳化硅性能对多孔SiC陶瓷/Zr基非晶合金复合材料的动态抗压强度都有较大影响,当多孔碳化硅孔隙率为23.77%,平均孔径尺寸为26.72um时,在复合材料制备浸渗温度为860℃,浸渗后保温6.0 min时,复合材料具有最高的动态抗压强度,为1757 MPa。多孔SiC陶瓷/Zr基非晶合金复合材料动态压缩断裂为脆性断裂,断口微观形貌特征包括SiC陶瓷相上形成具有不同特征的解理台阶,Zr基非晶合金相形成不同形态的脉状花样,非晶相保持相对完整。Zr基非晶合金相能有效阻碍裂纹的扩展,导致非晶相周围的碳化硅碎裂并挤压非晶相整体运动,从而提高了多孔SiC陶瓷/Zr基非晶合金复合材料动态抗压强度。
The research on the Dynamic Compressive Properties of Porous SiC Ceramic/ Zr-Base Amorphous Composites
英文关键词:porous  SiC ceramics, Zr-base  amorphous alloy , composite , dynamic  compression ,cleavage  step,veinpattern
英文摘要:
      The porous SiC ceramics / Zr-based amorphous alloy composites were prepared by the pressure - infiltration casting method. The influence of pressure - infiltration casting holding time and the properities of porous SiC ceramics on the dynamic compression performance were investigated with the split Hopkinson pressure bar (SHPB) and the S-4800 scanning electronic microscope (SEM). The results showed that The dynamic compressive strength of porous SiC ceramic /Zr based amorphous alloy composites was significantly affected by the holding time and the properties of porous SiC ceramic. The composited exhibited the highest dynamic compressive strength which was1757MPa with the porosity and Average aperture size were 23.77 and 26.72um, respectively, under the condition of the pressure - infiltration casting temperature and time were 860℃ and 6.0min, respectively. The fracture mode of the composite shows the brittle fracture under the dynamic compress load. The fracture morphology characteristics included the cleavage steps appear in ceramic with different characteristics and Different patterns of veins in Zr-base amorphous alloy kept in relatively intact. The Zr-based amorphous alloy can effectively hinder cracks expansion with the surrounding silicon carbide broke up and movement with amorphous alloys, which would improve the dynamic compressive strength of porous SiC ceramic / Zr-based amorphous composites.
作者单位E-mail
沈永华 北京理工大学 材料学院 shenyh1990@163.com 
张玉平 烟台大学 环境与材料工程学院 zhangyuping306@163.com 
程焕武 北京理工大学 材料学院 chenghuanwu@bit.edu.cn 
王扬卫 北京理工大学 材料学院  
王迎春 北京理工大学 材料学院  
李硕 北京理工大学 材料学院  
摘要点击次数: 26
全文下载次数: 32
查看全文  查看/发表评论  
关闭