易丽莎,张兴旺,林晓冬,姚美意,胡丽娟,李健健,梁雪,彭剑超,谢耀平,周邦新.Zr-0.75Sn-0.35Fe-0.15Cr-xNb合金在He+辐照下的显微组织演变及其对腐蚀行为的影响[J].稀有金属材料与工程,2023,52(4):1328~1337.[Yi Lisha,Zhang Xingwang,Lin Xiaodong,Yao Meiyi,Hu Lijuan,Li Jianjian,Liang Xue,Peng Jianchao,Xie Yaoping,Zhou Bangxin.Microstructural Evolution under He+ Irradiation and its Effect on Corrosion Behavior of Zr-0.75Sn-0.35Fe-0.15Cr-xNb Alloys[J].Rare Metal Materials and Engineering,2023,52(4):1328~1337.]
[doi]
Zr-0.75Sn-0.35Fe-0.15Cr-xNb合金在He+辐照下的显微组织演变及其对腐蚀行为的影响
投稿时间:2022-03-15  修订日期:2022-05-11
中文关键词:  锆合金,Nb含量,离子辐照,显微组织,氧化膜
基金项目:国家自然科学基金资助(52001192);
中文摘要:
      本工作采用2 MeV He+在300 ℃下对Zr-0.75Sn-0.35Fe-0.15Cr-xNb (x=0、1.0,wt%)合金进行辐照,然后在360 ℃/18.6 MPa/0.01 M LiOH水溶液中进行高压釜腐蚀实验,利用扫描电子显微镜和透射电子显微镜研究辐照对合金显微组织及腐蚀行为的影响。结果表明,添加Nb改变了Zr-0.75Sn-0.35Fe-0.15Cr合金中第二相的数量、尺寸和晶体结构。He+辐照1 dpa后,合金的辐照损伤峰区域分布有大量的He泡和型位错环,添加Nb对He泡和位错环的数量及第二相的元素扩散等均产生了一定的影响。腐蚀结果表明,He+辐照或添加1.0 wt%的Nb均可促进Zr-0.75Sn-0.35Fe-0.15Cr合金的腐蚀,但当二者同时存在时,辐照能减弱Nb促进腐蚀的作用。
Microstructural Evolution under He+ Irradiation and its Effect on Corrosion Behavior of Zr-0.75Sn-0.35Fe-0.15Cr-xNb Alloys
英文关键词:zirconium alloy,Nb content,ion irradiation, microstructure,oxide film
英文摘要:
      Zirconium alloys used as fuel claddings in water-cooled nuclear reactors generally serve in a harsh environment of high-temperature high-pressure water and strong neutron irradiation. Nb is known to play an important role in improving the corrosion resistance of zirconium alloys. Therefore, studying the microstructural changes and its effect on the corrosion behavior of zirconium alloys with different Nb contents before and after irradiation can provide a basis for the design of advanced zirconium alloys. In this work, Zr-0.75Sn-0.35Fe-0.15Cr-xNb (x=0, 1.0, wt%) alloys were prepared and irradiated with 2 MeV He+ at 300 ℃. The effects of irradiation on the microstructure and corrosion behavior of the alloys were investigated by using scanning electron microscope and transmission electron microscope. The corrosion environment was 360℃/18.6 MPa/0.01 M LiOH aqueous solution. The results revealed that the number, average size and crystal structure of the second phase particles in Zr-0.75Sn-0.35Fe-0.15Cr-xNb alloys changed with the increase of Nb content prior to irradiation. After He+ irradiation to 1 dpa, however, a large number of He bubbles and -type dislocation loops were induced in the radiation damage peak region in the alloys. To some extent, addition of Nb can affect the number of He bubbles and dislocation loops and elemental diffusion from the second phase particles. The corrosion results showed that He+ irradiation or addition of 1.0wt% Nb could accelerate the corrosion of Zr-0.75Sn-0.35Fe-0.15Cr alloy, but the irradiation could reduce the acceleration effect of Nb on the corrosion of Zr-0.75Sn-0.35Fe-0.15Cr alloy.
作者单位E-mail
易丽莎上海大学材料研究所 yilisha@shu.edu.cn 
张兴旺上海大学材料研究所 782496317@qq.com 
林晓冬* 上海大学材料研究所 xdlin@shu.edu.cn 
姚美意上海大学材料研究所  
胡丽娟上海大学材料研究所 lijuanhu@shu.edu.cn 
李健健中国科学院上海应用物理研究所 lijianjian@sinap.ac.cn 
梁雪上海大学微结构重点实验室 liangxue@shu.edu.cn 
彭剑超上海大学微结构重点实验室 jcpeng@shu.edu.cn 
谢耀平上海大学材料研究所 xieyp@shu.edu.cn 
周邦新上海大学材料研究所  
摘要点击次数: 360
全文下载次数: 213
查看全文   查看/发表评论    HTML
关闭