Large size Ti70 alloy ingot were manufactured by vacuum consumable arc melting(VAR) in this paper. The effect of melting rate on component homogeneity of Fe element was studied. Chemical composition of the ingots were measured by chemical composition analyser and compared with perp results. Micro area composition were detected with EDS. Microstructure of follow-up rolling plate was observed by a metalloscope and mechanical properties of the plate were tested by a tensile tester. The results show that the mush zone during solidification process of the ingot reducing and macrosegregation of Fe element decreasing with cutting down the melting rate to a stable level. Meanwhile, eutectic phase spacing narrowing down and microsegregation of Fe element alleviating with reducing the melting rate. The microstructure and tensile properties of the follow-up rolling plate compliancing with the standard requirements.