Microstructural variation and crack propagation of modified Ti Cr Si silicide coatings on the niobium alloy C 103 during oxidation at high temperatures in air have been studied. The results show that the crack propagation behavior is commonly determined by superficial glass phase, the silicon content of the body coating, and the growth and mechanical properties of low valent silicide.