Structures and Mechanical properties of a super-high strength Al-Li alloy
Affiliation:

School of Materials Science and Engineering,Central South University,,,School of Materials Science and Engineering,Central South University,School of Materials Science and Engineering,Central South University,Southwest Aluminum Group Co Ltd,Southwest Aluminum Group Co Ltd

  • Article
  • | |
  • Metrics
  • |
  • Reference [13]
  • |
  • Related [20]
  • | | |
  • Comments
    Abstract:

    The structures and mechanical properties of a new super-high strength Al-Li alloy developed by this group were investigated. The alloy possessed excellent properties, of which the tensile strength was greater than 600 MPa, and the elongation higher than 10%. After T8 aging, the strengthening precipitates in both cold-rolled sheet with 2 mm thickness and hot-rolled plate with 10 mm thickness were T1(Al2CuLi) and q¢(Al2Cu), and their fraction and size were basically same in the two plates with different thickness. The strength of T8-aged plate with 10 mm thickness was 50~70 MPa higher than that the T8-aged sheet with 2 mm thickness. This strength enhancement was originated from the texture fraction after solution treatment. The volume fraction of the deformation texture in the solutionized hot-rolled plate with 10 mm thickness was much higher.

    Reference
    [1] Zheng Zi-qiao(郑子樵), Li Jin-feng(李劲风),Chen Zhi-guo(陈志国), Li Hong-ying(李红英), Li Shi-chen(李世晨), Tan Cheng-yu(谭澄宇). Chinese Journal of Non-ferrous Metals(中国有色金属学报) [J]. 2011, 21(10): 2337-2349.
    [2] Li Jin-feng(李劲风), Zheng Zi-qiao(郑子樵), Chen Yong-lai(陈永来), et al. Aerospace Materials Technology(宇航材料工艺)[J]. 2012,42(1):13-19.
    [3] Wang Rui-qing(王瑞琴), Zheng Zi-qiao(郑子樵), ChenYuan-yuan(陈圆圆), et al. Rare Metals and Engineering(稀有金属材料与工程)[J], 2009, 38(4): 622-626.
    [4] Gault B, de Geuser F, Bourgeois L, et al. Ultramicroscopy[J]. 2011, 111: 683-689.
    [5] Kertz J E, GoumaA P I, Buchheit R G. Metallurgical and Materials Transactions A[J]. 2001, 32(10): 2561-2573.
    [6] Luo xian-fu(罗先甫), Zheng Zi-qiao(郑子樵), Zhong Ji-fa(钟继发), et al. Chinese Journal of Non-ferrous Metals(中国有色金属学报)[J]. 2013, 23(7):1833-1842
    [7] Li Jin-feng(李劲风), Chen Yong-lai(陈永来), Zhang Xu-hu(张绪虎), et al. Aerospace Materials Technology(宇航材料工艺)[J]. 2015,45(2):24-28
    [8] Li Jin-feng(李劲风), Liu Ping-li(刘平礼), Chen Yong-lai(陈永来), et al. Trans. Nonferrous Met. Soc. China [J]. 2015, 25(7): 2103?2112
    [9] Bunge H J. Texture analysis in materials science[M]. London: Butterworths Press. 1982: 88-106.
    [10] Tang J G, Zhang X M, Deng Y L, et al. Computational materials science[J]. 2006, 38(2): 395-399.
    [11] Yoshimura R, Konno T J, Abe E, et al. .Acta Materialia[J]. 2003, 51(14):4251-4266.
    [12] Nie J F, Muddle B C, Polmear I J. Materials Science Forum [J] 1996, 217: 1257-1262.
    [13] Y. Z. Shen, K. H. Oh, D. N. Lee. Scripta Materialia [J]. 2004, 51: 285-289.
    Cited by
    Comments
    Comments
    分享到微博
    Submit
Get Citation

[Li Jin-feng, Chen Yong-lai, Zhang Xu-hu, Liu Qing, Zheng Zi-qiao, Yao Yong, Wang Jian. Structures and Mechanical properties of a super-high strength Al-Li alloy[J]. Rare Metal Materials and Engineering,2017,46(12):3715~3720.]
DOI:[doi]

Copy
Article Metrics
  • Abstract:1562
  • PDF: 1255
  • HTML: 149
  • Cited by: 0
History
  • Received:September 28,2015
  • Revised:November 12,2015
  • Adopted:December 08,2015
  • Online: January 04,2018