Microstructure and Properties of Ti-15Mo Alloy with High Oxygen Content
Author:
Affiliation:

School of Materials Science and Engineering,Shenyang Aerospace University

Clc Number:

TG146.3

  • Article
  • | |
  • Metrics
  • |
  • Reference [20]
  • |
  • Related [20]
  • | | |
  • Comments
    Abstract:

    In this paper, the as-cast microstructure of Ti-15Mo alloy with high oxygen content and the microstructure and corresponding properties obtained by solution treatment at different temperatures are studied. Composition analysis shows that 0.8wt% O is dissolved in the alloy, hereinafter referred to as Ti-15Mo-0.8O alloy. The microstructure transformation of Ti-15Mo-0.8O alloy was observed and analyzed by optical microscope (OM), scanning electron microscope (SEM) and X-ray diffraction (XRD). The results show that the as-cast structure of the alloy consists of α and β phases. After solid solution treatment at 900℃, 1000℃, 1100℃/2h, the phase composition transformation process of the alloy is α+β+TOβ+TOβ; The lattice constant of β phase of alloy gradually increases with the increase of solid solution temperature. Hardness and room temperature compression tests were carried out by Vickers hardness tester and universal testing machine. The results show that the highest hardness of the sample after solution treatment at 1100℃/2h is 455HV20;The sample after solution treatment at 1100℃/2h has the best compression performance, with compressive yield strength of 1617Mpa and compressive strength of 2308Mpa respectively, and compression ratio of 22%.

    Reference
    [1] Leyens,C.(莱茵斯), Peters,M.(皮特尔斯). Titanium and Titanium Alloys(钛与钛合金)[M].北京:化学工业出版社, 2005:1-429
    [2] Alves A P R , Santana F A , Rosa L A A , et al. Materials Science Engineering C[J], 2004, 24(5):693-696.
    [3] Min X H , Emura S , Sekido N , et al. Materials Science Engineering: A[J], 2010, 527(10-11):2693-2701.
    [4] Zhang J Y , Li J S , Chen Z , et al. Journal of Alloys and Compounds[J], 2017, 699:775-782.
    [5] Min X H , Tsuzaki K , Emura S , et al. Materials Science Engineering: A [J], 2011, 528(13-14):4569-4578.
    [6] Xiang Li(向 力), Min Xiaohua(闵小华), Mi Guangbao(弭光宝)et al. Materials Engineering(材料工程)[J], 2017, 45(7): 128-136
    [7] Wei L S , Kim H Y , Miyazaki S . Acta Materialia[J], 2015, 100:313-322.
    [8] Furuta T , Kuramoto S , Morris J W , et al. Scripta Materialia[J], 2013, 68(10):767-772.
    [9] Li Qiang(李强), Ma Dong(马东), Zhou Kai(周凯) et al. Nonferrous Metal Materials and Engineering(有色金属材料与工程)[J], 2017, 38(6) :351-355
    [10] Min X H , Xang L , Li M , et al. Acta Metallurgica Sinica -Chinese Edition-[J], 2018, 54(9):1262-1272.
    [11] Min X H, Bai P F, Emura S, et al. Mater. Sci. Eng.[J], 2017, A684: 534
    [12] Yin F , Iwasaki S , Ping D , et al. Advanced Materials[J], 2010, 18(12):1541-1544.
    [13] Wang Qingjuan(王庆娟), Gao Qi (高颀), Wang Dingchun (王鼎春)et al. Thermal processing technology(热加工工艺)[J],2014,43(6):50-52.
    [14] Banerjee, Dipankar. Scripta Materialia[J], 2017, 141:146-147.
    [15] Ezaki H , Morinaga M , Yukawa N , et al. Philosophical Magazine A[J], 1992, 65(5):1249-1260.
    [16] Wang Liqiang(王立强). Shanghai Jiaotong University(上海交通大学)[D], 2009.
    [17] Kuroda D , Niinomi M , Morinaga M , et al. Materials Science and Engineering A[J], 1998, 243(1-2):244-249.
    [18] Li Ping(李萍), Jiang Zheng(江政), Yuan Baoguo(袁宝国) et al. Journal of Plastic Engineering(塑性工程学报)[J], 2012, 19(6):15
    [19] Xiang Li(向 力). Dalian University of Technology(大连理工大学)[D], 2017
    [20] Sadeghpour S , Abbasi S M , Morakabati M , et al. Journal of Alloys and Compounds[J], 2018,746:206-217
    Cited by
    Comments
    Comments
    分享到微博
    Submit
Get Citation

[WANG Yanjing, XU Zaidong, Xu Rongzheng, Hu Qiuye, Shi Dongyu, Lu Xin. Microstructure and Properties of Ti-15Mo Alloy with High Oxygen Content[J]. Rare Metal Materials and Engineering,2020,49(7):2425~2430.]
DOI:10.12442/j. issn.1002-185X.20190548

Copy
Article Metrics
  • Abstract:852
  • PDF: 1178
  • HTML: 152
  • Cited by: 0
History
  • Received:June 28,2019
  • Revised:July 31,2019
  • Adopted:August 21,2019
  • Online: August 31,2020