Effect of deformation conditions on hot deformation and corrosion behavior of as-extruded ZA21 magnesium alloy
Author:
Affiliation:

Engineering Technology Research Institute,University of Science Technology Beijing

Clc Number:

Fund Project:

Fundamental Research Funds for the Central Universities(No.2302018FRF-IC-18-004)

  • Article
  • |
  • Figures
  • |
  • Metrics
  • |
  • Reference
  • |
  • Related
  • |
  • Cited by
  • |
  • Materials
  • |
  • Comments
    Abstract:

    In this paper, the effects of deformation temperature, strain rate and deformation on the hot deformation behavior and microstructure of as-extruded ZA21 magnesium alloy were investigated. The processing map was established, and the immersion weight loss and electrochemical tests were carried out on the unstable zone, the safe zone and the best processing zone to study the corrosion behavior in different regions of ZA21 magnesium alloy. The results show that the dynamic softening mechanism of ZA21 magnesium alloy is mainly dynamic recovery at high temperature and low strain rate, and dynamic recrystallization is dominant at low temperature and high strain rate; The optimum processing temperature is 300~350 °C, and the strain rate is 0.001~0.01s-1, which is mainly related to the generation of complete dynamic recrystallization; Under the same processing technology, with the increase of deformation, the self-corrosion potential of ZA21 magnesium alloy is obviously positively shifted, and the self-corrosion current density is significantly decreased. When the amount of deformation increases to 60%, the self-corrosion current density can be reduced by 3~4 orders of magnitude. This is mainly because the grain refinement leads to a denser oxide film on the surface of the alloy; However , the microstructure of the processing instability zone has wedge cracks and obvious pores, so the corrosion rate is relatively large.

    Reference
    Related
    Cited by
Get Citation

[Panpan Wang, Haitao Jiang, Yujiao Wang, Yun Zhang, Bowen Yu, Binbin Zhong, Zhiming Cao. Effect of deformation conditions on hot deformation and corrosion behavior of as-extruded ZA21 magnesium alloy[J]. Rare Metal Materials and Engineering,2020,49(10):3544~3551.]
DOI:10.12442/j. issn.1002-185X.20190894

Copy
Article Metrics
  • Abstract:
  • PDF:
  • HTML:
  • Cited by:
History
  • Received:October 29,2019
  • Revised:November 09,2019
  • Adopted:November 12,2019
  • Online: November 04,2020
  • Published: