Near-α titanium alloy and Ti₂AlNb alloy powders premixed with different proportions were prepared on the near-α titanium alloy substrate by laser deposition technique, and the microstructure characteristics were analyzed and discussed. Results show that numerous river-like sub-grain structures are formed inside the equiaxed B2 grains of the laser-deposited premixed titanium alloy powders with the proportion of Ti₂AlNb above 40wt%, whereas the needle-like structure within coarse columnar β grains exist with the proportion of Ti₂AlNb below 40wt%. It is noteworthy that the decrease in laser power and scanning speed can accelerate the formation of sub-grain structures. Based on the analysis of experimental results, it can be inferred that the formation of sub-grain structure not only is related to the precipitation of O phase due to composition micro-segregation at sub-grain boundaries, but also is inseparable from the stacking faults caused by the internal stress during the laser deposition.