郭廷彪,王晨,李琦,张锋,贾智.单晶铜ECAP/Bc路径形变结构与力学性能[J].稀有金属材料与工程(英文),2018,47(10):3096~3103.[guotingbiao,wangchen,liqi,zhangfeng and jiazhi.Deformation Structure and Mechanical Properties of Single Crystal Copper Deformed by Route Bc ECAP[J].Rare Metal Materials and Engineering,2018,47(10):3096~3103.]
Deformation Structure and Mechanical Properties of Single Crystal Copper Deformed by Route Bc ECAP
Download Pdf  View/Add Comment  Download reader
Received:December 29, 2016  Revised:May 04, 2017
DOI:
Key words: equal channel angular pressing  electron backscattered diffraction  texture  single crystal copper
Foundation item:国家自然科学基金资助(项目号51261016)
Author NameAffiliation
guotingbiao,wangchen,liqi,zhangfeng and jiazhi  
Hits: 27
Download times: 6
Abstract:
      The deformation structure of single crystal copper during 4 passes equal channel angular pressing (ECAP) througth route Bc were investigated by electron backscatter diffraction (EBSD) and XRD methods, and the mechanical properties of the deformed material were measured. The results show that the macroscopic orientation of single crystal under low pass deformation was not changed. After 2 passes,orientation-ordered shear bands appeared and inclined at angles in the range of 15°–20°from the ED direction,deformation texture {111}<112> appeared on grains;After 4 passes,the angle between the shear band and the ED direction was constant , the inclined direction was opposite to that of the 2 passes,the texture of the material was still in texture of {111}<112>,and large angle grain boundary was not presented;The tensile strength increased from 168MPa to 395MPa, the elongation decreased from 63% to 26.5%, the material hardness increased from 60Hv to 125Hv and then was tended to be changed little. Because of dislocation accumulation, the plastic deformation capability of the material becomes worse and the necking area increases. ECAP has positive effect on enhanceing the strength of single crystal copper with not broken grains.