陈冬.U-Nb合金中夹杂物的纳米压痕表征[J].稀有金属材料与工程(英文),2019,48(1):165~170.[Chen Dong.Nanoindentation characterization of inclusions in U-Nb alloy[J].Rare Metal Materials and Engineering,2019,48(1):165~170.]
Nanoindentation characterization of inclusions in U-Nb alloy
Download Pdf  View/Add Comment  Download reader
Received:May 17, 2017  Revised:August 25, 2017
DOI:
Key words: U-5.5Nb alloy  nanoindentation  inclusions  mechanical property
Foundation item:中国工程物理研究院重点项目(项目号TB120301)
Author NameAffiliation
Chen Dong  
Hits: 30
Download times: 2
Abstract:
      Mechanical properties of the Nb2C and U(N,C) inclusions and matrix in the U-5.5Nb alloy are characterized by nanoindentation and the yield strength and plasticity index are calculated from the obtained hardness. The result from experiment shows that the Nb2C inclusion has the highest elastic modulus and hardness, while the corresponding values of the U(N,C) inclusion are far less than those in the Nb2C inclusion but higher than matrix. Moreover, the result calculated from hardness shows that the yield strength of the Nb2C inclusion is the highest, but the plasticity index is the lowest, which reveals that the Nb2C inclusion inclines to elastic deformation. However, the yield strength of the U(N,C) inclusion is low and the plasticity index of the U(N,C) is the highest, which reveals that the U(N,C) inclusion prefers to plastic deformation and also can broke easily. Elastic modulus and hardness from multi-cycle load/unload test are close to those obtained by single load/unload test, in addition, the elastic modulus obtained from nanoindentation is accord to the value obtained by tensile test in the literature.