顾玉芬.铜/钨异种金属A-TIG电 弧点焊工艺及性能研究[J].稀有金属材料与工程(英文),2019,47(3):947~952.[顾玉芬.Research on process and performance of Cu/W dissimilar Metal welded by A-TIG arc spot welding[J].Rare Metal Materials and Engineering,2019,47(3):947~952.]
Research on process and performance of Cu/W dissimilar Metal welded by A-TIG arc spot welding
Download Pdf  View/Add Comment  Download reader
Received:July 25, 2017  Revised:August 10, 2017
DOI:
Key words: TIG spot welding  activating flux  macroscopic feature  microstructure  tensile strength
Foundation item:国家自然科学基金项目(51675256) 兰州理工大学红柳杰出人才培养计划(J201201)
Author NameAffiliation
顾玉芬  
Hits: 7
Download times: 3
Abstract:
      Due to the connection problem of Cu/W during the rolling process of tungsten plate, dissimilar metals Cu/W are welded by Tungsten inert gas(TIG) welding.In the case of coating SiO2 and uncoating SiO2 activating flux,the spot welding of W overlapped by Cu was conducted,respectively,the appearance of spot welding,cross-section,microstructure and tensile strength of joints were analyzed,respectively.The results indicate that top surface of the welding spots uncoated SiO2 are convex and irregular,many holes at the interface,in the case of coating SiO2,the center of welding spot appears round pits,the number of holes at interface reduce.Interdiffusion occurs between Cu and W,the interface of samples coated with SiO2 is more tightness than the uncoated. When the welding current is same,the strength of joint coated with SiO2 are higher than the uncoated,in the two cases of welding ,fracture exists a large different.