向雪梅.617B镍基高温合金长期时效组织演变[J].稀有金属材料与工程(英文),2019,47(3):865~872.[xiangxuemei.Microstructure Evolution of Long-Term Aged 617B Ni-based Superalloy[J].Rare Metal Materials and Engineering,2019,47(3):865~872.]
Microstructure Evolution of Long-Term Aged 617B Ni-based Superalloy
Download Pdf  View/Add Comment  Download reader
Received:August 01, 2017  Revised:September 06, 2017
DOI:
Key words: Ni-based superalloy  long-term aging  microstructure evolution
Foundation item:国家重点研发计划(项目号2017YFB0305201)
Author NameAffiliation
xiangxuemei  
Hits: 37
Download times: 45
Abstract:
      617B is a solid-solution strengthened Ni-based superalloy, a candidate material for 700℃ A-USC power plant. It is always used in solution-anneal at about 700℃. So it is significant to research its microstructure evolution during aging at its service temperature rang form 650℃ to 750℃. In this work, the 617B alloy was exposed prolonged approximately 3000h at 650℃, 700℃, 750℃ respectively. The microstructure evolution had been characterized by optical microscope (OM), field emission scanning electron microscope (FESEM) and energy dispersive spectrometer (EDS). γ" phase and Cr, Mo-rich M23C6 were the major precipitates during aging treatment. γ" phase precipitated at about 650℃,600h and got coarsening with a prolonged time and an increasing temperature. The coarsening of γ" phase met the LSW theory below 700℃ aging but when exposed higher than 750℃, it was priority to coarsen by agglomeration. The carbides along grain boundaries were transformed into continuous network structure by the gradual coarsening of small serration carbides. And carbides within grains increased during aging. When alloy undergone 750℃ long-term aged, there are reactions between carbides, matrix and γ"phase.