吴俊峰,邹世坤,巩水利,车志刚,曹子文.超高应变率激光冲击不同厚度Al7050合金的层裂研究[J].稀有金属材料与工程(英文),2019,48(4):1096~1101.[wu Junfeng,Zou Shikun,Gong Shuili,Che Zhigang and Cao Ziwen.Spall of different thicknesses Al7050 alloy under ultrahigh strain rate laser shock peening[J].Rare Metal Materials and Engineering,2019,48(4):1096~1101.]
Spall of different thicknesses Al7050 alloy under ultrahigh strain rate laser shock peening
Download Pdf  View/Add Comment  Download reader
Received:October 29, 2017  Revised:December 07, 2017
DOI:
Key words: Al7050 alloy  laser shock peening  spall mechanism  spall threshold  spall fracture morphology
Foundation item:国家重点专项(2016YFB1102705)
Author NameAffiliation
wu Junfeng,Zou Shikun,Gong Shuili,Che Zhigang and Cao Ziwen  
Hits: 12
Download times: 2
Abstract:
      The spall characteristics of different thicknesses Al7050 alloy treated by laser shock peening (LSP) with different process parameters (Process-1 and Process-2) were investigated to obtain the spall mechanism and spall threshold. The particle velocity of rear free surface and spall crater morphology in 0.33 mm thickness Al7050 induced by LSP with Process-1 were measured and analyzed by a Photonic Doppler Velocimetry (PDV) system and scanning electron microscope (SEM), respectively. Spall sizes, spall thicknesses and spall fracture morphology in 5 mm thickness Al7050 induced by LSP with Process-2 were analyzed by a C-scan ultrasonic nondestructive testing with water immersion, optical microscope (OM) and SEM, respectively. The results indicated that spall strength and LSP strain rate of 0.33 mm thickness Al7050 were calculated by PDV data. Spall crater morphology was also analyzed in detail. Spall sizes of 5 mm thickness Al7050 increased with continued multiple LSP impacts and its spall thicknesses were in range from 343 μm to 364 μm. Spall mechanism was mixture ruptures of ductile behavior with spherical voids and brittle behavior with straight cracks. Continued LSP-5 was the spall threshold of 5 mm thickness Al7050. Compared with as-received material, the micro-hardness of 5 mm thickness Al7050 with continued LSP-5 increased in the surface layer and decreased near rear free surface. The results provided not only some important insights on the spall behavior of aluminum alloy with laser shock but also fundamental research for avoiding the spall in industrial applications.