徐高磊,彭丽军,米绪军,解浩峰,黄国杰,杨振,冯雪,尹向前,刘冬梅.上引-连续挤压法制备Cu-Cr-Ag合金组织性能的研究[J].稀有金属材料与工程(英文),2019,48(4):1310~1316.[XuGaolei,PengLijun,Mixujun,XIEHaofemh,Huangguojie,yangzhen,Fengxue,Yinxiangqiang and LiuDongmei.Microstructure and Properties of Cu-Cr-Ag alloy fabricated by up-drawn continuous casting and continuous extrusion[J].Rare Metal Materials and Engineering,2019,48(4):1310~1316.]
Microstructure and Properties of Cu-Cr-Ag alloy fabricated by up-drawn continuous casting and continuous extrusion
Download Pdf  View/Add Comment  Download reader
Received:December 17, 2017  Revised:February 02, 2018
DOI:
Key words: Cu-Cr-Ag alloy  Up-drawn continuous casting and continuous extrusion  Aging treatment  Microstructure  Physical properties
Foundation item:国家重点研发计划项目(2016YFB0301400),国家自然科学基金(项目号:51601017和51401026)
Author NameAffiliation
XuGaolei,PengLijun,Mixujun,XIEHaofemh,Huangguojie,yangzhen,Fengxue,Yinxiangqiang and LiuDongmei  
Hits: 50
Download times: 22
Abstract:
      Effect of aging treatment on microstructure and properties of Cu-Cr-Ag alloy fabricated by up-drawn continuous casting and continuous extrusion are investigated by scanning electron microscopy (SEM) and transmission electron microscopy (TEM). The results show that the grains were refined significantly, with an average size of 4~5 μm, when the cast rob was processed during the continuous extrusion. The relation curve between Vickers hardness and aging time firstly rapid decrease, then quickly raise, finally slowly decrease and the electrical conductivity firstly rapid increase, then slowly raise, finally trended to stable as the aging time rise, when the Cu-Cr-Ag alloy was solutioned at 875℃ for 1h, 60% cold deformation and aged at 450℃ for different time, respectively. The precipitation sequence of Cu-Cr-Ag alloy aged at 450 ℃ is supersaturated solid sloution→G.P zones→fcc Cr phase→order fcc Cr phase→bcc Cr phase. The orientation relationship between bcc Cr precipitates and the matrix exhibit NW-OR