张聪惠,杨军,宋国栋,任海涛.超声喷丸对工业纯锆拉拉疲劳性能的影响研究[J].稀有金属材料与工程(英文),2019,48(6):1954~1960.[zhangconghui,yangjun,songguodong and renhaitao.Effect of ultrasonic peening on tensile-tensile fatigue properties of industrial pure zirconium[J].Rare Metal Materials and Engineering,2019,48(6):1954~1960.]
Effect of ultrasonic peening on tensile-tensile fatigue properties of industrial pure zirconium
Download Pdf  View/Add Comment  Download reader
Received:May 03, 2018  Revised:June 11, 2018
DOI:
Key words: USSP, Roughness, Fatigue  property, Fracture  morphology
Foundation item:国家自然科学基金资助(项目号51674187)
Author NameAffiliation
zhangconghui,yangjun,songguodong and renhaitao  
Hits: 16
Download times: 3
Abstract:
      Ultrasonic shot peening (USSP) was used to treat industrial pure zirconium and its tension-tension fatigue properties were studied. The microstructure and surface hardness of the samples were characterized by optical microscopy (OM) and microhardness tester. The grain size, micro distortion and residual stress of sample surface were analyzed by X ray diffractometer (XRD). The results show that:After USSP treatment, the grain size is refined to the nano scale, and the residual compressive stress, surface roughness and hardness of the surface increase with USSP time. The fatigue limit of original industry pure zirconium is 195MPa, USSP treatment can significantly increase the fatigue limit and the maximum fatigue limit of USSP treated 45min is maximum, reaching 220MPa, which is 11.2% higher than original industrial pure zirconium. The lower the maximum loading stress during fatigue loading is, the increase of fatigue life by USSP treatment is more obvious.