Microstructure and Mechanical Properties of Rolled and Annealed Mg-Y-Zr-xNd Alloys
DOI:
Author:
Affiliation:

College of Materials Science and Engineering, Chongqing University

Clc Number:

Fund Project:

National Key R&D Program of China,The National Natural Science Foundation of China (General Program, Key Program, Major Research Plan),The Fundamental Research Funds for the Central Universities

  • Article
  • |
  • Figures
  • |
  • Metrics
  • |
  • Reference
  • |
  • Related
  • |
  • Cited by
  • |
  • Materials
  • |
  • Comments
    Abstract:

    Microstructures and mechanical properties of Mg-5Y-0.6Zr-xNd (x=0, 0.5 and 1wt.%) alloys under various heat treatment conditions were investigated by optical microstructure (OM), scanning electron microscope (SEM), X-ray diffraction (XRD), electron backscatter diffraction (EBSD) and tensile tests. Results showed that with increasing content of Nd, the amount of second phases Mg24Y5 and Mg14Nd2Y (β) was increased in the matrix. Minor Nd addition can reduce the stacking fault energy of α-Mg and promote the dynamic recrystallization during hot-rolled process. As the Nd content increases, the volume fraction of static recrystallization was promoted obviously. The average grain size of Mg-5Y-0.6Zr-0Nd alloy after annealed treatment can be refined to 3.73 μm. Tensile strength of as-rolled alloys increased with the addition of Nd, while the elongation exhibited an opposite change tendency. As-rolled alloy sheet with 1.01 wt.% Nd exhibited the remarkable mechanical properties, which the values of ultimate tensile strength, yield strength and elongation were 336 MPa, 278 MPa and 16.3%, respectively. Based on the microstructure observation, the changes of mechanical properties have been discussed.

    Reference
    Related
    Cited by
Get Citation

[Dai Yan, Chen Xianhua, Xu Xiaoyang, Zhao Chaoyue, Liu Chunquan, Zhao Di, Liu Xiaofang, Luo Zhu, Tu Teng, Pan Fusheng. Microstructure and Mechanical Properties of Rolled and Annealed Mg-Y-Zr-xNd Alloys[J]. Rare Metal Materials and Engineering,2019,48(7):2099~2106.]
DOI:[doi]

Copy
Article Metrics
  • Abstract:
  • PDF:
  • HTML:
  • Cited by:
History
  • Received:June 21,2018
  • Revised:September 12,2018
  • Adopted:September 13,2018
  • Online: August 01,2019
  • Published: