王彦峰,李争显,杜继红,张长伟.TC4钛合金表面渗碳复合TiN(Ti)膜层的抗冲蚀性能研究[J].稀有金属材料与工程(英文),2019,48(6):1878~1883.[Yanfeng Wang,Zhengxian Li,Jihong Du and Changwei Zhang.Solid particle erosion of composite coating of gradient carburized layer and TiN(Ti) coating synthesized on TC4 alloy[J].Rare Metal Materials and Engineering,2019,48(6):1878~1883.]
Solid particle erosion of composite coating of gradient carburized layer and TiN(Ti) coating synthesized on TC4 alloy
Download Pdf  View/Add Comment  Download reader
Received:July 12, 2018  Revised:August 14, 2018
DOI:
Key words: plasma  carburization, Ti/TiN  coating, solid  particle erosion, multilayered  structure, toughness
Foundation item:科技部中乌国际合作项目,2014DFR50450
Author NameAffiliation
Yanfeng Wang,Zhengxian Li,Jihong Du and Changwei Zhang  
Hits: 21
Download times: 6
Abstract:
      Solid particle erosion (SPE) resistance of compressor titanium alloy blade can be enhanced by the hard coatings. But the system of hard coating / soft substrate is easily corrupt by the SPE due to the coatings’ higher brittleness and interface mismatch, so the brittle fracture often occurs at the interface of coating and substrate. In order to improve the hard coatings’ SPE resistance, combining with the plasma ion diffusion and arc ion plating technology, a series of composite coatings with gradient carburized layer and TiN(Ti) coating were synthesized on TC4 alloy. And the influence of structure on composite coating’s properties was studied in detail. The results showed that the hardness and bonding strength of composite coatings were enhanced remarkably, comparing with the monolayer TiN and 12 periods of Ti/TiN hard coatings deposited on TC4 alloy without plasma carburization. The monolayer TiN showed a mechanism of brittle cracking after sand erosion, and the 12 periods of Ti/TiN coating presents morphologies of flaking and erosion pit due to the multilayer toughening effect. After carburization, the coating’s impact toughness was enhanced. The interface fracture of monolayer TiN was restrained. And the composite coating with gradient carburized layer and 12 periods of Ti/TiN coating possessed the best SPE resistance with erosion weight loss rate decreased by more than ten times and showed a mechanism of tough damage, which can be attributed to its higher interface strength and better match of hardness and toughness.