卢振洋,龚文韬,陈树君,袁涛,李晓旭.7475铝合金回填式FSSW接头微观组织与力学性能研究[J].稀有金属材料与工程(英文),2019,48(4):1267~1274.[Lu Zhenyang,Gong Wentao,Chen Shujun,Yuan Tao and Li xiaoxu.MICROSTRUCTURE AND FAILURE MECHANISMS OF REFILL FRICTION STIR SPOT WELDED 7475 ALUMINUM ALLOY JOINTS[J].Rare Metal Materials and Engineering,2019,48(4):1267~1274.]
MICROSTRUCTURE AND FAILURE MECHANISMS OF REFILL FRICTION STIR SPOT WELDED 7475 ALUMINUM ALLOY JOINTS
Download Pdf  View/Add Comment  Download reader
Received:September 12, 2018  Revised:September 28, 2018
DOI:
Key words: Refilled FSSW Welding  Microstructure  Technological Parameter  Fracture Mode
Foundation item:国家自然科学基金No.51704013和中国博士后基金No.2016M600881
Author NameAffiliation
Lu Zhenyang,Gong Wentao,Chen Shujun,Yuan Tao and Li xiaoxu  
Hits: 55
Download times: 14
Abstract:
      The 7475 aluminum alloy backfill friction stir spot welding is studied in this paper. Firstly, the 2mm 7475 aluminum alloy is welded by different process parameters, then the surface and cross section of the joint are observed, and the hardness and tensile shear test of the sample are carried out. The results show that the joint can be divided into four parts according to the weld microstructure, and the grain size of different parts is different. Hook, holes and unjointed microstructures due to poor fluidity of the material are found in the microstructure. At the same time, the hardness of the base metal zone and stirring zone is significantly higher than that of the heat affected zone and the thermo-mechanically affected zone; in addition, the highest hardness and tensile shear strength of the joint vary with welding tool rotation speed land the depth of the sleeve. However, the effect of the stirring sleeve movement rate on the mechanical properties of the solder joint is not obvious.