邓莉萍,鲁世强,汤斌兵.热暴露对Cr-12Nb-4.4Ni合金组织及性能的影响[J].稀有金属材料与工程(英文),2019,48(12):4068~4073.[Deng Liping,Lu Shiqiang and Tang Binbing.Effect of Thermal Exposure on Microstruture and Properties of Cr-12Nb-4.4Ni Alloy[J].Rare Metal Materials and Engineering,2019,48(12):4068~4073.]
Effect of Thermal Exposure on Microstruture and Properties of Cr-12Nb-4.4Ni Alloy
Download Pdf  View/Add Comment  Download reader
Received:September 13, 2018  Revised:October 20, 2018
DOI:
Key words: Chromium-base alloy  Laves phase  thermal exposure  Ni  crystal defects
Foundation item:国家自然科学基金(51074092),江西省自然科学基金(20161BAB206113),江西省教育厅落地计划项目(KJLD14056),江西省教育厅科技计划(GJJ160677)
Author NameAffiliation
Deng Liping,Lu Shiqiang and Tang Binbing  
Hits: 19
Download times: 7
Abstract:
      The Cr-12Nb-4.4 Ni alloy, prepared by mechanical alloying and hot pressing, was thermally exposed at 1200℃ for 30, 50 and 100 h, respectively. Then, the microstructure and properties of the thermally exposed Cr-12Nb-4.4Ni alloy were studied. The results show that the phase constituent is stable during the thermal exposure process. It consists of Cr solid solution (Crss) and NbCr2, and Ni is mainly presented in NbCr2. Grain size of Crss increases with the thermal exposure time, while grain size of NbCr2 particle has no obvious change. The NbCr2 structure becomes loose due to the replacement of Cr by Ni. The increase of compressive stress in the phase interface of Cr/NbCr2 promotes the emergence of dislocations in Cr matrix and the increase of stacking fault/ twinning fault in NbCr2 particles. With the thermal exposure time, the compressive strength, yield strength and plastic strain of the Cr-12Nb-4.4 Ni alloy decrease slightly while the alloy still remains relatively high room temperature strength and good plastic during the thermal exposure process. After thermal exposure for 100h, the compressive strength, yield strength and plastic strain are 2170MPa, 1406MPa and 9.5%, respectively. The Cr-12Nb-4.4 Ni alloy can keep good fracture toughness after thermal exposure for 100h.