田浩亮,王长亮,郭孟秋,汤智慧,高俊国,崔永静,魏世丞,徐滨士.爆炸喷涂石墨烯改性涂层的工艺及自润滑耐磨机制研究[J].稀有金属材料与工程(英文),2020,49(3):1058~1067.[TIAN Hao–liang,WANG Chang–liang,GUO Meng–qiu,TANG Zhi–hui,GAO Jun–guo,CUI Yong–jing,WEI Shi-cheng and XU Bin-shi.Study on Prepare ProcessTechnology and Self-lubrication and Wear Resistance Mechanism of Graphene Modified Coating by Detonation Spraying[J].Rare Metal Materials and Engineering,2020,49(3):1058~1067.]
Study on Prepare ProcessTechnology and Self-lubrication and Wear Resistance Mechanism of Graphene Modified Coating by Detonation Spraying
Download Pdf  View/Add Comment  Download reader
Received:February 28, 2019  Revised:March 27, 2019
DOI:
Key words: powder milling process  detonation gun spraying  graphene  self-lubricating  wear resistance
Foundation item:国家自然科学基金资助(51605455)
Author NameAffiliation
TIAN Hao–liang,WANG Chang–liang,GUO Meng–qiu,TANG Zhi–hui,GAO Jun–guo,CUI Yong–jing,WEI Shi-cheng and XU Bin-shi  
Hits: 47
Download times: 3
Abstract:
      Aiming to reduce the friction coefficient of WC-12Co wear-resistant coating, the self-lubricating coating was developed by adding graphene to WC–Co coating deposited via detonation gun spraying. In this study, four powder processes, including wet ball milling, wet mixing, spray granulation, and sintering and crushing, were used to obtaingraphene/WC–Co composite powders. The presence, microstructure and phase composition of graphene in powder and coating were analyzed by means of SEM, EDS and Raman. The mechanical properties of the coating were studied by the microhardness tester and the universal tensile machine. When the spray granulation process is used to prepare the composite powder, a greater amount of graphene covers the surface of the WC–Copowder, and the transparent thin-layered structure of the graphene remains unchanged. The bonding strength and hardness of the resultant coating are approximately 68 MPa and 940 HV0.3, respectively. Graphene modification causes a 25% reduction in the friction coefficient. During the friction process, the graphene constantly forms a lubricating film that serves as an excellent self-lubricating layer.