奉隆彪,黎小辉,宋旭东,袁鸽成,卢凤池.Mg-1Zn-1Gd合金在等径角挤压下的晶粒细化机理及织构演变[J].稀有金属材料与工程(英文),2020,49(10):3325~3331.[Feng Longbiao,Li Xiaohui,Song Xudong,Yuan Gecheng and Lu Fengchi.Grain Refinement and Texture Evolution of Mg-1Zn-1Gd Alloy by the Equal Channel Angular Pressing[J].Rare Metal Materials and Engineering,2020,49(10):3325~3331.]
Grain Refinement and Texture Evolution of Mg-1Zn-1Gd Alloy by the Equal Channel Angular Pressing
Download Pdf  View/Add Comment  Download reader
Received:August 16, 2019  Revised:October 06, 2019
DOI:
Key words: Mg-Zn-Gd alloy  Equal Channel Angular Pressing  grain refinement  DRX  texture
Foundation item:国家自然科学基金项目(面上项目,重点项目,重大项目)
Author NameAffiliation
Feng Longbiao,Li Xiaohui,Song Xudong,Yuan Gecheng and Lu Fengchi  
Hits: 12
Download times: 19
Abstract:
      In this paper, in order to find out the effect of Equal Channel Angular Pressing (ECAP) on the microstructure and texture, as well as dynamic recrystallization (DRX) behavior, Mg-1Zn-1Gd alloy (wt.%) was investigated. The results show that after the equal channel angular pressing at 350℃, the microstructures of these samples is composed of fine recrystallized grains, and there are a large number of homogeneously distributed equiaxed grains in the matrix. Upon 8 passes, the uniform ultra-fine grain structure with an average grain size of 3.6 μm is obtained. The mechanism of the discontinuous dynamic recrystallization (DDRX) and continuous dynamic recrystallization (CDRX) lead to grain refinement. The micro-texture was analyzed through electron backscatter diffraction (EBSD) technique. It is revealed that after 4 passes of ECAP, a strong basal texture is achieved (multiple?random?distribution?~19.76). With the extrusion passes increasing, the grain in the basal planes of extruded alloy billet is mainly elongated along the extrusion direction, the orientation distribution changes from concentrated state to decentralized state. The texture is weakened which the maximum strength is 15.66 mrd. Finally, the texture is also related to the plane anisotropy of the Mg-1Zn-1Gd alloy.