储林华,袁改焕,姚美意,高博,徐诗侗,周邦新.杂质元素(C,Si)对Zr-4合金板材试样微观结构及腐蚀性能的影响[J].稀有金属材料与工程(英文),2020,49(10):3338~3346.[Chu Linhua,Yuan Gaihuan,Yao Meiyi,Gao Bo,Xu Shitong and Zhou Bangxin.Effect of Impurity Elements(C, Si) on the Microstructure and Corrosion Resistance of Zircaloy-4 Sheet Samples by TEM, XPS and 3DAP[J].Rare Metal Materials and Engineering,2020,49(10):3338~3346.]
Effect of Impurity Elements(C, Si) on the Microstructure and Corrosion Resistance of Zircaloy-4 Sheet Samples by TEM, XPS and 3DAP
Download Pdf  View/Add Comment  Download reader
Received:August 18, 2019  Revised:September 05, 2019
DOI:
Key words: Zircaloy, impurity, microstructure, uniform corrosion, β-solution treatment, second phase particles, agglomerate
Foundation item:
Author NameAffiliation
Chu Linhua,Yuan Gaihuan,Yao Meiyi,Gao Bo,Xu Shitong and Zhou Bangxin  
Hits: 12
Download times: 16
Abstract:
      In the range of ASTM, the effect of impurity elements on microstructure and corrosion resistance of Zr-4 alloy were studied by using sheet samples. The results show that reducing carbon content and increasing silicon content are beneficial to uniform corrosion performance of Zr-4 alloy at 400℃ steam. Microscopic analysis shows that carbon is easily enriched in the form of Zr-C on the matrix phase, and its content mainly affects the corrosion resistance by affecting the precipitation of second phase particles. The lower its content is, the easier it is to form the parallel plate (PP) structure during quenching, and the higher its content is, the more likely it is to form basketweave (BW) structure, while the second phase particles are easier to precipitate along the grain boundary of PP structure. When quenching temperature is lower than 1200℃, silicon content has no obvious effect on the formation of PP structure. Meanwhile, three-dimensional atom probe (3DAP) analysis shows that silicon tends to agglomerate in the form of SiO2 around the second phase particles, delays or weaken the oxidation of second phase particles, thus improving the corrosion resistance of Zr-4 alloy.