信云鹏,朱知寿,王新南,李明兵,刘格辰,李静,商国强,祝力伟.高速弹丸冲击诱发TC32钛合金中绝热剪切带的组织演化行为[J].稀有金属材料与工程(英文),2020,49(10):3361~3368.[Yunpeng Xin,Zhishou Zhu,Xinnan Wang,Mingbing Li,Gechen Liu,Jing Li,Guoqiang Shang and Liwei Zhu.Microstructural evolution behavior of adiabatic shear bands induced by high-speed projectile impact in TC32 titanium alloy[J].Rare Metal Materials and Engineering,2020,49(10):3361~3368.]
Microstructural evolution behavior of adiabatic shear bands induced by high-speed projectile impact in TC32 titanium alloy
Download Pdf  View/Add Comment  Download reader
Received:September 09, 2019  Revised:October 30, 2019
DOI:
Key words: adiabatic shear band  nanocrystal  amorphous  TC32 titanium alloy
Foundation item:
Author NameAffiliation
Yunpeng Xin,Zhishou Zhu,Xinnan Wang,Mingbing Li,Gechen Liu,Jing Li,Guoqiang Shang and Liwei Zhu  
Hits: 16
Download times: 8
Abstract:
      The microstructure characterization and evolution behavior of TC32 titanium alloy after high-speed projectile impact were studied by optical microscope (OM), scanning electron microscope (SEM) and transmission electron microscopy (TEM). The distribution of adiabatic shear band(ASB) and stress around the crater has always been a semi-circular diffusion. The rotating refinement process of large equiaxed grains and elongated lath subgrains in adiabatic shear band was observed. Focus ion beam (FIB) technology was used to accurately prepare TEM samples from the crack tip in the ASB. It was found that the coexistence of the amorphous regions, the amorphous-to-crystalline transition regions, the fine-scale nano-crystalline region around the crack tip. The calculation proved that the temperature rise in ASB could cause microstructure melting, the amorphous regions and small size nanocrystals were formed after fast quenching. Because the microstructure in the ASBs is fine equiaxed grains and amorphous with higher strength, the area between the deformed band and matrix is relatively weakened, and it is found that the initiation of cracks in adiabatic shear bands is mainly concentrated at the junction of deformed band and matrix, and the crack propagate in the form of microvoids rotation coupling.