闫宁,宋文,张玉梅.退火对镁阳极氧化涂层结构与耐腐蚀性能的影响[J].稀有金属材料与工程(英文),2020,49(6):2168~2174.[Yan Ning,Song Wen and Zhang Yumei.Effect of annealing on structure and corrosion resistance of magnesium anodized coating[J].Rare Metal Materials and Engineering,2020,49(6):2168~2174.]
Effect of annealing on structure and corrosion resistance of magnesium anodized coating
Download Pdf  View/Add Comment  Download reader
Received:December 28, 2019  Revised:April 16, 2020
DOI:
Key words: magnesium  annealing  structure  corrosion resistance  biocompatibility
Foundation item:国家自然科学基金重点项目(81530051,31670966,31800790)
Author NameAffiliation
Yan Ning,Song Wen and Zhang Yumei  
Hits: 26
Download times: 0
Abstract:
      Objective: To optimize the anodized film on the magnesium surface and explore its effect on the structure,corrosion resistance and biocompatibility through anodizing and annealing treatments.Methods: Pure magnesium was anodized with different voltage parameters (5V, 10V, 20V, 40V), and then annealed at high temperature. The surface and cross-section morphology of the coatings formed were analyzed by scanning electron microscopy.Three-dimensional structure and roughness were analyzed by atomic force microscope. The corrosion behavior of each group of samples was evaluated by electrochemical polarization experiments and in vitro immersion test.The proliferation activity of mouse osteoblasts MC3T3-E1 was evaluated by the CCK-8 method. Results: The increase of the voltage can make the surface coating become porous from the lamellar shape, and then continue to increase voltage,the layer become smooth and uniform. The annealing treatment maintained the basic morphological characteristics, the coating thickness increased and the roughness decreased.The corrosion resistance of the unannealed coating does not increase due to the existence of micropores and the instability of magnesium hydroxide. The dense magnesium oxide crystalline coating formed by the annealing has a certain protective effect. The 40V post-oxidation annealing group has relatively good corrosion resistance and has no obvious inhibitory effect on cell proliferation.Conclusion: Voltage affects the structure of anodized coating. Annealing can further stabilize the coating and improve its corrosion resistance.The 40V post-oxidation annealing group has a better corrosion resistance and biocompatibility .